Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 13.0 µm/m-°C @Temperature 100 °C |
7.22 µin/in-°F @Temperature 212 °F |
|
Outokumpu 4501 Duplex Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto) form. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 230® alloy, 20% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 230® alloy, 30% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 230® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 230® alloy, 40% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 95.0 °C |
7.22 µin/in-°F @Temperature 77.0 - 203 °F |
|
Haynes HR-160® alloy plate, aged 4000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 95.0 °C |
7.22 µin/in-°F @Temperature 77.0 - 203 °F |
|
Haynes HR-160® alloy, annealed plate Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 230® alloy, plate, 8000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 700 °C |
7.22 µin/in-°F @Temperature 77.0 - 1290 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 700 °C |
7.22 µin/in-°F @Temperature 77.0 - 1290 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed and 40% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 21.0 - 100 °C |
7.22 µin/in-°F @Temperature 69.8 - 212 °F |
Mean; aged |
Special Metals DURANICKEL® 301 (UNS N03301) Annealed Wire Tensile strength (ultimate) and elongation values reported here are typical for Annealed Wire specifically. Other property values are typical of annealed DURANICKEL® alloy 301 or the alloy in gen.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 21.0 - 100 °C |
7.22 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
Special Metals DURANICKEL® 301 (UNS N03301) Cold-Drawn and Aged Rod and Bar Tensile strength (ultimate and yield), compressive strength, hardness, and elongation values reported here are typical for Cold-Drawn and Aged Rod and Bar specifically. Other property values are typ.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 21.0 - 100 °C |
7.22 µin/in-°F @Temperature 69.8 - 212 °F |
Mean; aged |
Special Metals DURANICKEL® 301 (UNS N03301) Spring Wire Tensile strength (ultimate) and elongation values reported here are typical for Spring Wire specifically. Other property values are typical of annealed DURANICKEL® alloy 301 or the alloy in gener.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 21.0 - 100 °C |
7.22 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
Special Metals INCONEL® 725 Nickel Superalloy (UNS N07725) Age Hardened Strip Tensile strength (ultimate and yield), hardness, impact, and elongation values reported here are typical for Age Hardened Strip samples. Other property values are typical of INCONEL® alloy 725.D.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 21.0 - 100 °C |
7.22 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
Special Metals INCONEL® 725 Nickel Superalloy (UNS N07725), Age Hardened Round Tensile strength (ultimate and yield), hardness, impact, and elongation values reported here are typical for Age Hardened Round samples. Other property values are typical of INCONEL® alloy 725.D.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 21.0 - 100 °C |
7.22 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
Special Metals INCONEL® 725 Nickel Superalloy (UNS N07725), Age Hardened Tube Tensile strength (ultimate and yield), hardness, and elongation values reported here are typical for Age Hardened Tube samples. Other property values are typical of INCONEL® alloy 725.Data provi.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 21.1 - 427 °C |
7.25 µin/in-°F @Temperature 70.0 - 800 °F |
|
Crucible Steel Nitriding #135 Modified Steel, AISI 4140 Modified Nitriding #135 steel is a modification of AISI 4140 specifically designed to be nitrided for high surface hardness and abrasion resistance.Information provided by Crucible Industries |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 21.0 - 427 °C |
7.22 µin/in-°F @Temperature 69.8 - 801 °F |
|
Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Condition H 1150 (Heated 621°C) Data provided by Carpenter Technology Corporation.Custom 630 (17Cr-4Ni) is a martensitic precipitation/age-hardening stainless steel offering high strength and hardness along with excellent corrosio.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 230® alloy, GMAW deposit weld metal Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 230® alloy, hot rolled and 1232°C solution annealed plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 230® alloy, plate, 1000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 20.0 - 700 °C |
7.22 µin/in-°F @Temperature 68.0 - 1290 °F |
|
Carpenter Hampden® High Carbon, High Chrome Tool Steel (Oil-Wear) (AISI D3) Hampden tool steel is an oil-hardening, high-carbon, high-chromium die steel having extreme wear resistance, It hardens with very little change in size or shape. Hampden tool steel is a deep-hardeni.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 100 °C |
7.22 µin/in-°F @Temperature 212 °F |
|
Outokumpu LDX 2101® Duplex Stainless Steel Applications: Pulp and paper industryDesalination plantsFlue-gas cleaningCargo tanks and pipe systems in chemical tankersSeawater systemsFirewalls and blast walls on offshore platformsBridgesCompone.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 230® alloy plate, 8000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 230® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 230® alloy, as cast vacuum investment casting Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 230® alloy, plate, 4000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |