- Polymer Property : CTE, linear = 7.22 µin/in-°F
Polymer Property : CTE, linear = 7.22 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.0 µm/m-°C @Temperature -55.0 - 288 °C |
7.22 µin/in-°F @Temperature -67.0 - 550 °F |
X, Y- Direction; ASTM D3386-94 |
| Rogers Corporation RO3206 Woven-Glass Reinforced PTFE Laminate Features and Benefits:Woven glass reinforcement - Improves rigidity for easier handlingUniform electrical and mechanical performance - ideal for complex multi-layer high frequency structuresLow diel.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 20.0 °C |
7.22 µin/in-°F @Temperature 68.0 °F |
Across Surface; ASTM D-696 |
| Glastic GLASTHERM HT220 Insulation Sheet Glastherm Grade HT220 is a thermal insulation sheet that is a highly heat-resistant material that combines low thermal conductivity with very high compressive strength at molding temperature. It is.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 20.0 °C |
7.22 µin/in-°F @Temperature 68.0 °F |
Across Surface; ASTM D-696 |
| Glastic GLASTHERM HT250 Insulation Sheet Glastherm Grade HT250 is a high compressive strength, heat-resistant composite material. It is ideal for insulation between the fold and the press or within the mold itself. Grade HT250 is asbesto.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 230® alloy plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 230® alloy plate, 4000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 230® alloy, 10% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 230® alloy, 30% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 230® alloy, 30% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 95.0 °C |
7.22 µin/in-°F @Temperature 77.0 - 203 °F |
|
| Haynes HR-160® alloy, annealed plate Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 95.0 °C |
7.22 µin/in-°F @Temperature 77.0 - 203 °F |
|
| Haynes HR-160® alloy, plate, aged 1000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 95.0 °C |
7.22 µin/in-°F @Temperature 77.0 - 203 °F |
|
| Haynes HR-160® alloy, plate, aged 4000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 700 °C |
7.22 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed and 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 21.0 - 100 °C |
7.22 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
| Special Metals DURANICKEL® 301 (UNS N03301) Annealed and Aged Strip Tensile strength (ultimate), hardness, and elongation values reported here are typical for Annealed and Aged Strip specifically. Other property values are typical of aged DURANICKEL® alloy 301 or.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 21.0 - 100 °C |
7.22 µin/in-°F @Temperature 69.8 - 212 °F |
Mean; aged |
| Special Metals DURANICKEL® 301 (UNS N03301) Annealed Rod and Bar Tensile strength (ultimate and yield), compressive strength, hardness, and elongation values reported here are typical for Annealed Rod and Bar specifically. Other property values are typical of ann.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 21.0 - 100 °C |
7.22 µin/in-°F @Temperature 69.8 - 212 °F |
Mean; aged |
| Special Metals DURANICKEL® 301 (UNS N03301) Annealed Strip Tensile strength (ultimate and yield), hardness, and elongation values reported here are typical for Annealed Strip specifically. Other property values are typical of annealed DURANICKEL® alloy 3.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 21.0 - 100 °C |
7.22 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
| Special Metals DURANICKEL® 301 (UNS N03301) Cold-Drawn and Aged Rod and Bar Tensile strength (ultimate and yield), compressive strength, hardness, and elongation values reported here are typical for Cold-Drawn and Aged Rod and Bar specifically. Other property values are typ.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 21.0 - 100 °C |
7.22 µin/in-°F @Temperature 69.8 - 212 °F |
Mean; aged |
| Special Metals DURANICKEL® 301 (UNS N03301) Spring Strip Tensile strength (ultimate), hardness, and elongation values reported here are typical for Spring Strip specifically. Other property values are typical of annealed DURANICKEL® alloy 301 or the al.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 21.0 - 100 °C |
7.22 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
| Special Metals DURANICKEL® 301 (UNS N03301) Spring Wire, Aged Tensile strength (ultimate) and elongation values reported here are typical for Spring Wire, Aged specifically. Other property values are typical of aged DURANICKEL® alloy 301 or the alloy in gen.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 20.0 - 500 °C |
7.22 µin/in-°F @Temperature 68.0 - 932 °F |
|
| Schmolz + Bickenbach Thermodur® 2999 Hot Work Die Steel Description: Maximum high-temperature strength, good high-temperature wear resistance, excellent thermal shock resistance and thermal conductivity across the entire range of service temperatures App.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 20.0 - 600 °C |
7.22 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| Bohler-Uddeholm BÖHLER S601 (M2 Modified) High Speed Steel For Cold Work Applications Properties: Tungs ten-molybdenum high speed steel with ex cel lent toughness and cut ting proper ties, for a wide variety of uses.Applications: Taps, twist drills, reamers, broaching tools, meta.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 20.0 - 800 °C |
7.22 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Carpenter No. 610® High Carbon, High Chrome Tool Steel (Air-Wear) (AISI D2) No. 610 tool steel is an air hardening, high-carbon, high-chromium tool steel having extremely high wear resisting properties. It is very deep hardening, and will be practically free from size chang.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 20.0 - 400 °C |
7.22 µin/in-°F @Temperature 68.0 - 752 °F |
|
| Assab Steels CALMAX Plastic Mold Material CALMAX is a chromium-molybdenum-vanadium alloyed steel characterized by:High toughnessGood wear resistanceGood through hardening propertiesGood dimensional stability in hardeningGood polishabilityGo.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 230® alloy, GMAW deposit weld metal Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 230® alloy, hot rolled and 1232°C solution annealed plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 230® alloy, 50% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 230® alloy, as cast vacuum investment casting Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 13.0 µm/m-°C @Temperature 25.0 - 200 °C |
7.22 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 230® alloy, plate, 4000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||