- Polymer Property : CTE, linear = 15.0 µm/m-°C
Polymer Property : CTE, linear = 15.0 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.0 µm/m-°C @Temperature 100 - 200 °C |
8.33 µin/in-°F @Temperature 212 - 392 °F |
Axial; ISO 11359-2 |
| Chevron Phillips Ryton® R-7-220NA Polyphenylene Sulfide Resin
(discontinued **) Ryton® R-7-220 is a glass and mineral filled polyphenylene sulfide compound developed to provide good mechanical strength and enhanced hydrolytic stability in applications requiring constant or rep.. |
|||
| CTE, linear | 15.0 µm/m-°C @Temperature -50.0 - 50.0 °C |
8.33 µin/in-°F @Temperature -58.0 - 122 °F |
Axial; ASTM E831 |
| Solvay Specialty Polymers Ryton® R-4-230NA Polyphenylene Sulfide Compound
(Unverified Data**) Natural Color Polyphenylene Sulfide CompoundRyton® R-4-230NA is an advanced 40% fiberglass reinforced polyphenylene sulfide compound which provides reduced flash and improved processability compare.. |
|||
| CTE, linear | 15.0 µm/m-°C @Temperature 0.000 - 500 °C |
8.33 µin/in-°F @Temperature 32.0 - 932 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.0 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 15.0 µm/m-°C @Temperature 0.000 - 500 °C |
8.33 µin/in-°F @Temperature 32.0 - 932 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.7 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 15.0 µm/m-°C @Temperature 0.000 - 500 °C |
8.33 µin/in-°F @Temperature 32.0 - 932 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 15.0 µm/m-°C @Temperature 20.0 - 100 °C |
8.33 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Industeel URANUS® B6 N Multipurpose Austenitic Stainless Steel with PREN = 36 Description: URANUS® B6 (904L) is a multipurpose 20 Cr - 4.3 Mo high corrosion resistance austenitic stainless steel developed 40 years ago by CLI. The UR B6N is alloyed with nitrogen (~ 0.13%) t.. |
|||
| CTE, linear | 15.0 µm/m-°C @Temperature 25.0 - 1000 °C |
8.33 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed, 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 15.0 µm/m-°C @Temperature 0.000 - 500 °C |
8.33 µin/in-°F @Temperature 32.0 - 932 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 3.2 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 15.0 µm/m-°C @Temperature 25.0 - 1000 °C |
8.33 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 242® alloy Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 15.0 µm/m-°C @Temperature 25.0 - 1000 °C |
8.33 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 242® alloy, after 4000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 15.0 µm/m-°C @Temperature 25.0 - 1000 °C |
8.33 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 242® alloy, after 8000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 15.0 µm/m-°C @Temperature 25.0 - 1000 °C |
8.33 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed and 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 15.0 µm/m-°C @Temperature 25.0 - 1000 °C |
8.33 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed and 40% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 15.0 µm/m-°C @Temperature 20.0 - 300 °C |
8.33 µin/in-°F @Temperature 68.0 - 572 °F |
|
| Schott N-PK52A Glass Suitable for precision moldingInformation Provided by SCHOTT North America, Inc. |
|||
| CTE, linear | 15.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
8.33 µin/in-°F @Temperature 73.4 - 176 °F |
longitudinal; ASTM E831 |
| Bond Laminates TEPEX® dynalite 102-RG600(x)/47% Roving Glass – PA 6 Consolidated Composite Laminate Within the TEPEX® composite laminate, Polyamide 6 is a resin known for its toughness, stiffness, abrasion resistance, heat and chemical resistances. Roving E-Glass fibers have an excellent impact .. |
|||
| CTE, linear | 15.0 µm/m-°C @Temperature 20.0 - 200 °C |
8.33 µin/in-°F @Temperature 68.0 - 392 °F |
|
| ATI Allegheny Ludlum Martensitic Stainless Steel Type 440A, Hardened + 482°C Temper Allegheny Ludlum Type 440A is a hardenable straight-chromium stainless steel which combines superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stainle.. |
|||
| CTE, linear | 15.0 µm/m-°C @Temperature 100 - 200 °C |
8.33 µin/in-°F @Temperature 212 - 392 °F |
Axial; ISO 11359-2 |
| Solvay Specialty Polymers Ryton® R-7-121NA Polyphenylene Sulfide Resin
(Unverified Data**) Ryton® R-7-121NA is an advanced glass/mineral filled polyphenylene sulfide compound developed to provide good mechanical strength with good flow and low maintenance molding using conventional moldi.. |
|||
| CTE, linear | 15.0 µm/m-°C @Temperature 20.0 - 250 °C |
8.33 µin/in-°F @Temperature 68.0 - 482 °F |
|
| Resistalloy International Resistalloy 8020 Nickel Chromium Electrical Resistance Alloy Used mainly for electrical elements in both industrial and domestic applications. Industrial applications vary from small laboratory kilns to heavy-duty heat-treatment furnaces under all types of at.. |
|||