Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 188 alloy, 0% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 188 alloy, hot rolled and 1175°C solution annealed plate Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 188 alloy, plate at RT after 4000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 200 °C |
6.61 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Bar, Hot Rolled and Solution Annealed HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 200 °C |
6.61 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Shielded Metal Arc Welded (SMAW) Plate HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 0.000 - 100 °C |
6.61 µin/in-°F @Temperature 32.0 - 212 °F |
|
Kennametal Stellite Stellite® 12 PM cast Applications: include vane plugs, fuel metering pins, spacer bushings, ball blanks (bearings), race blanks (bearings), diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous wea.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 300 °C |
6.61 µin/in-°F @Temperature 68.0 - 572 °F |
|
Industeel TENASTEEL® Cold Work Tool Steel Description: TENASTEEL is a cold work tool steel, combining a high wear resistance together with a very high toughness. Its other advantages are a good machinability in the as-delivery condition and.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 100 °C |
6.61 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 188 alloy, cold rolled and 1175°C solution annealed sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 400 °C |
6.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 242® alloy Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 400 °C |
6.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 242® alloy, after 1000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 400 °C |
6.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 242® alloy, after 4000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 400 °C |
6.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 400 °C |
6.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed and 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 204 °C |
6.61 µin/in-°F @Temperature 68.0 - 399 °F |
|
Haynes Hastelloy® C-4 alloy, all-weld metal, as welded, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 200 °C |
6.61 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Sheet, Cold Rolled and Solution Annealed HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 25.0 - 200 °C |
6.61 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 787 °C |
6.61 µin/in-°F @Temperature 68.0 - 1450 °F |
|
ATI Allegheny Ludlum 430 Ferritic Stainless Steel Characteristics:oxidation resistant at elevated temperatures, corrosion resistance approaching nickel-bearing stainless steels in mildly corrosive environments, ductile, does not work harden readily.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 787 °C |
6.61 µin/in-°F @Temperature 68.0 - 1450 °F |
|
ATI Allegheny Ludlum AL 403™ Martensitic Stainless Steel Characteristics: corrosion resistant, heat resistant, oxidation resistant up to 1400°F.Information provided by Allegheny Ludlum |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 900 °C |
6.61 µin/in-°F @Temperature 68.0 - 1650 °F |
|
ATI Allegheny Ludlum Type 441 Alloy Stainless Steel Allegheny Ludlum stainless Type 441 alloy is a heat resisting ferritic grades providing good oxidation and corrosion resistance for applications like automotive exhaust system components. Dual stab.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 300 °C |
6.61 µin/in-°F @Temperature 68.0 - 572 °F |
|
Bohler-Uddeholm BÖHLER W360 ISOBLOC® Hot Work Tool Steel BÖHLER W360 ISOBLOC was developed as a tool steel for dies and punches in warm and hot forging. The steel can be used for a variety of applications where hardness and toughness are required. Prope.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 21.0 - 93.0 °C |
6.61 µin/in-°F @Temperature 69.8 - 199 °F |
|
Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Condition H 1150 (Heated 621°C) Data provided by Carpenter Technology Corporation.Custom 630 (17Cr-4Ni) is a martensitic precipitation/age-hardening stainless steel offering high strength and hardness along with excellent corrosio.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 21.0 - 93.0 °C |
6.61 µin/in-°F @Temperature 69.8 - 199 °F |
|
AK Steel 15-5 PH® Precipitation Hardening Stainless Steel, Condition H 1150 AK Steel 15-5 PH® provides high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C), and good toughness in both base metal and welds. Short-time, .. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 204 °C |
6.61 µin/in-°F @Temperature 68.0 - 399 °F |
|
Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 10 hours at 649°C (1200°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
CTE, linear | 11.9 µm/m-°C @Temperature 20.0 - 204 °C |
6.61 µin/in-°F @Temperature 68.0 - 399 °F |
|
Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |