Polymer Property : CTE, linear = 8.39 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, cold worked sheet, 15% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 26.0 - 649 °C |
8.39 µin/in-°F @Temperature 78.8 - 1200 °F |
|
| Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 26.0 - 649 °C |
8.39 µin/in-°F @Temperature 78.8 - 1200 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 538°C (1000°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 26.0 - 649 °C |
8.39 µin/in-°F @Temperature 78.8 - 1200 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 649°C (1200°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 26.0 - 649 °C |
8.39 µin/in-°F @Temperature 78.8 - 1200 °F |
|
| Haynes Ultimet® alloy, all-weld metal, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 26.0 - 649 °C |
8.39 µin/in-°F @Temperature 78.8 - 1200 °F |
|
| Haynes Ultimet® alloy, plate, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, cold rolled and 1205°C (2200°F) solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, room temperature sheet after 100 hours of 760°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, vacuum investment castings, solution treated Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 0% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 537°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, bar, after 0 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 24.0 - 500 °C |
8.39 µin/in-°F @Temperature 75.2 - 932 °F |
Mean |
| Special Metals INCONEL® G-3 Nickel Superalloy Data provided by the manufacturer, Special Metals. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 649 °C |
8.39 µin/in-°F @Temperature 77.0 - 1200 °F |
|
| Carpenter Stentor® Alloy Tool Steel (Oil-Hard) (AISI 02) An oil-hardening alloy with excellent size change properties, Stentor tool steel is especially suited for general purpose work in the toolroom. It is safe to harden, and shows little size change or .. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 26.0 - 538 °C |
8.39 µin/in-°F @Temperature 78.8 - 1000 °F |
|
| ATI Allegheny Ludlum Altemp® HX Nickel-Based superalloy Characteristics: outstanding resistance to oxidation at high temperatures, exceptional strength at elevated temperatures, good fabricability, good machinability in annealed condition, work hardening.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, room temperature after 0% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 20% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 40% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 21.0 - 538 °C |
8.39 µin/in-°F @Temperature 69.8 - 1000 °F |
|
| Kennametal Stellite Stellite® 31 PM cast aged 8 hours at 802°C air cooled Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous we.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||