Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 133 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	133 °C	271 °F	Edgew 120104 sp=100mm; ISO 75/Be
SABIC Innovative Plastics Lexan® 124R PC (Europe-Africa-Middle East) Low viscosity, multi purpose polycarbonate resin with added release agent. FDA food contact compliant in limited colors. Effective January 15th, 2007 this grade will no longer be supported with bi..
Deflection Temperature at 0.46 MPa (66 psi)	133 °C @Thickness 3.20 mm	271 °F @Thickness 0.126 in	unannealed; ASTM D 648
SABIC Innovative Plastics Lexan® DMX9455 PC Copolymer Lexan* DMX9455 is a standard flow, flame retardant, V0/1.5mm, opaque polycarbonate copolymer resin with improved scratch resistance.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 0.46 MPa (66 psi)	133 °C	271 °F	Edgew 120104 sp=100mm; ISO 75/Be
SABIC Innovative Plastics Lexan® FXE121R PC (Europe-Africa-Middle East) LEXAN FXE121R is a transparent/translucent low viscosity grade for special effects colors with a fluorescent appearance. Color package may affect performance.
Deflection Temperature at 0.46 MPa (66 psi)	133 °C	271 °F	Edgew 120104 sp=100mm; ISO 75/Be
SABIC Innovative Plastics Lexan® FXG121R PC (Europe-Africa-Middle East) LEXAN FXG121R is a transparent/translucent low viscosity grade for special effects colors with a diamond sparkle appearance. Color package may affect performance.
Deflection Temperature at 0.46 MPa (66 psi)	133 °C	271 °F	Edgew 120104 sp=100mm; ISO 75/Be
SABIC Innovative Plastics Lexan® FXM171R PC (Europe-Africa-Middle East) LEXAN FXM171R is a transparent/translucent high flow grade for special effects colors with a metallic-luster appearance. Color package may affect performance.
Deflection Temperature at 0.46 MPa (66 psi)	133 °C	271 °F	Edgew 120104 sp=100mm; ISO 75/Be
SABIC Innovative Plastics Lexan® HP1R PC (Europe-Africa-Middle East) High flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO sterilizable. Contains a higher amount o..
Deflection Temperature at 0.46 MPa (66 psi)	133 °C	271 °F	Edgew 120104 sp=100mm; ISO 75/Be
SABIC Innovative Plastics Lexan® HPS1 PC High flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, e-beam and gamma sterilizable. Contains..
Deflection Temperature at 0.46 MPa (66 psi)	133 °C	271 °F	Edgew 120104 sp=100mm; ISO 75/Be
SABIC Innovative Plastics Lexan® HPS1R PC (Asia Pacific) High flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, e-beam and gamma sterilizable. Contains..
Deflection Temperature at 0.46 MPa (66 psi)	133 °C	271 °F	Edgew 120104 sp=100mm; ISO 75/Be
SABIC Innovative Plastics Lexan® HPS2 PC (Europe-Africa-Middle East) Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, e-beam and gamma sterilizable..
Deflection Temperature at 0.46 MPa (66 psi)	133 °C	271 °F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics Lexan® IR1810 PC (Europe-Africa-Middle East) IR1810 resin is a high flow (MFR = 22 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold release.
Deflection Temperature at 0.46 MPa (66 psi)	133 °C @Thickness 3.20 mm	271 °F @Thickness 0.126 in	ASTM D648
SABIC Innovative Plastics Lexan® IR1810 PC (Europe-Africa-Middle East) IR1810 resin is a high flow (MFR = 22 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold release.
Deflection Temperature at 0.46 MPa (66 psi)	133 °C	271 °F	Edgew 120104 sp=100mm; ISO 75/Be
SABIC Innovative Plastics Lexan® LUX2110T_ PC (Europe-Africa-Middle East) Global grade. LEXAN LUX2110T is an injection moulding grade especially designed for manufacturing optical parts requiring easy flow properties combined with very high transmission and color stabilit..
Deflection Temperature at 0.46 MPa (66 psi)	133 °C	271 °F	Edgew 120104 sp=100mm; ISO 75/Be
SABIC Innovative Plastics Lexan® LUX2910T_ PC (Europe-Africa-Middle East) Global grade. LEXAN LUX2910T is an injection moulding grade especially designed for manufacturing optical parts requiring superior flow properties combined with very high transmission and color stab..
Deflection Temperature at 0.46 MPa (66 psi)	133 °C	271 °F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics Lexan® PC2200R PC (Europe-Africa-Middle East) PC2200R resin is a high flow (MFR = 22 at 300?C/1.2kg), heat stabilized, polycarbonate product with mold release designed for use in the general purpose molding market.
Deflection Temperature at 0.46 MPa (66 psi)	133 °C @Thickness 3.20 mm	271 °F @Thickness 0.126 in	ASTM D648
SABIC Innovative Plastics Lexan® PC2200R PC (Europe-Africa-Middle East) PC2200R resin is a high flow (MFR = 22 at 300?C/1.2kg), heat stabilized, polycarbonate product with mold release designed for use in the general purpose molding market.
Deflection Temperature at 0.46 MPa (66 psi)	133 °C @Thickness 3.20 mm	271 °F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics Lexan® DMX9455A PC Copolymer (Asia Pacific) This product will be phased out per January 2015 -- Lexan* DMX9455A is a standard flow, flame retardant, transparent polycarbonate copolymer resin with improved scratch resistance.
Deflection Temperature at 0.46 MPa (66 psi)	133 °C	271 °F	Edgew 120104 sp=100mm; ISO 75/Be
SABIC Innovative Plastics Lexan® HF1140 PC Ideal for disposables/short life cycles. Good clarity, heat resistance, property retention and dimensional stability. FDA food contact compliant in limited colors.Effective January 15th, 2007 this..
Deflection Temperature at 0.46 MPa (66 psi)	133 °C	271 °F	Edgew 120104 sp=100mm; ISO 75/Be
SABIC Innovative Plastics Lexan® HF1140 PC (Europe-Africa-Middle East) Ideal for disposables/short life cycles. Good clarity, heat resistance, property retention and dimensional stability. FDA food contact compliant in limited colors.Effective January 15th, 2007 this..
Deflection Temperature at 0.46 MPa (66 psi)	133 Â°C	271 Â°F	ISO 75-1,-2
Inno-Comp INNOPOLÂ® CS 1-5140 BLH 40% Talc-Filled Polypropylene Homopolymer INNOPOLÂ® CS 1-5140 BLH is a 40% talc-filled polypropylene homopolymer compound /PP-H TD40 (ISO 1043)/.INNOPOLÂ® CS 1-5140 BLH is recommended especially for producing products, where high stiffn..
Deflection Temperature at 0.46 MPa (66 psi)	133 Â°C @Thickness 6.40 mm	271 Â°F @Thickness 0.252 in	unannealed; ASTM D648
SABIC Innovative Plastics NORYL PX9406 PPE+PS Nonbrominated, nonchlorinated, flame retarded. Improved productivity and reliability. 252F HDT. UL94 V-0 rated. Electrical applications.
Deflection Temperature at 0.46 MPa (66 psi)	133 Â°C @Thickness 3.20 mm	271 Â°F @Thickness 0.126 in	ASTM D 648
SABIC Innovative Plastics PC2200 PC (Asia Pacific) PC2200 resin is a high flow (MFR = 22 at 300ÂºC/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold release..
Deflection Temperature at 0.46 MPa (66 psi)	133 Â°C @Thickness 3.20 mm	271 Â°F @Thickness 0.126 in	ASTM D648
SABIC Innovative Plastics PC2200 PC (Europe-Africa-Middle East) PC2200 resin is a high flow (MFR = 22 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold release.
Deflection Temperature at 0.46 MPa (66 psi)	133 Â°C @Thickness 3.20 mm	271 Â°F @Thickness 0.126 in	ASTM D 648
SABIC Innovative Plastics PC2200R PC (Asia Pacific) PC2200R resin is a high flow (MFR = 22 at 300ÂºC/1.2kg), heat stabilized, polycarbonate product with mold release designed for use in the general purpose molding market.This data was supplied by S..
Deflection Temperature at 0.46 MPa (66 psi)	133 Â°C @Thickness 3.20 mm	271 Â°F @Thickness 0.126 in	ASTM D 648
SABIC Innovative Plastics PC2200R PC (Europe-Africa-Middle East) PC2200R resin is a high flow (MFR = 22 at 300ÂºC/1.2kg), heat stabilized, polycarbonate product with mold release designed for use in the general purpose molding market.This data was supplied by S..
Deflection Temperature at 0.46 MPa (66 psi)	133 Â°C @Thickness 3.20 mm	271 Â°F @Thickness 0.126 in	ASTM D648
SABIC Innovative Plastics PC2203R PC (Asia Pacific) PC2203R resin is a high flow (MFR = 22 at 300?C/1.2kg), heat and UV stabilized, polycarbonate product with mold release designed for use in the general purpose molding market.
Deflection Temperature at 0.46 MPa (66 psi)	133 Â°C @Thickness 3.20 mm	271 Â°F @Thickness 0.126 in	ASTM D648
SABIC Innovative Plastics PC2800 PC (Europe-Africa-Middle East) PC2800 resin is a high flow (MFR = 28 at 300Â°C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold release...
Deflection Temperature at 0.46 MPa (66 psi)	133 Â°C	271 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP THERMOCOMP 9X02540 PC+PET LNP* THERMOCOMP* PDX-02540 is a compound based on a PET+PC Blend containing Proprietary Filler. Flame Retardant.
Deflection Temperature at 0.46 MPa (66 psi)	133 Â°C @Thickness 3.20 mm	271 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics NORYL NF2020 PPE+PS (Asia Pacific)
Deflection Temperature at 0.46 MPa (66 psi)	133 °C	271 °F	ISO 75-1,-2
Covestro Makrolon® ET UV540 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• PC/UV absorber concent..
Deflection Temperature at 0.46 MPa (66 psi)	133 °C	271 °F
Polimeri Europa KOBLEND PCA 839 PC+ABS (discontinued **) Symbol according to ISO 1043/1: PC+ABS Injection moulding grade with very good impact behaviour even at low temperatures, good dimensional stability. Vicat/B50 = 130°C Main applications fields: a..