SABIC Innovative Plastics Lexan® DMX9455A PC Copolymer (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® DMX9455A PC Copolymer (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This product will be phased out per January 2015 -- Lexan* DMX9455A is a standard flow, flame retardant, transparent polycarbonate copolymer resin with improved scratch resistance.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Density 1.17 g/cc
0.0423 lb/in³
ASTM D792
1.17 g/cc
0.0423 lb/in³
ISO 1183
Water Absorption 0.080 %

@Time 86400 sec
0.080 %

@Time 24.0 hour
ASTM D570
Moisture Absorption 0.0400 %
0.0400 %
50% RH, 24 hrs; ASTM D570
0.130 %
0.130 %
23°C / 50% RH; ISO 62
Moisture Absorption at Equilibrium 0.13 %
0.13 %
50% RH; ASTM D570
0.28 %
0.28 %
ASTM D570
Water Absorption at Saturation 0.27 %
0.27 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 14.5 g/10 min

@Load 1.20 kg,
Temperature 300 °C
14.5 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 13 g/10 min

@Load 1.20 kg,
Temperature 300 °C
13 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell L 108
108
ASTM D785
Hardness, Rockwell M 93
93
ASTM D785
Hardness, H358/30 128 MPa
18600 psi
ISO 2039-1
Tensile Strength at Break 60.0 MPa
8700 psi
50 mm/min; ISO 527
65.0 MPa
9430 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 80.0 MPa
11600 psi
Type I, 50 mm/min; ASTM D638
80.0 MPa
11600 psi
50 mm/min; ISO 527
Elongation at Break 40 %
40 %
50 mm/min; ISO 527
70 %
70 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 7.0 %
7.0 %
Type I, 50 mm/min; ASTM D638
7.0 %
7.0 %
50 mm/min; ISO 527
Tensile Modulus 2.45 GPa
355 ksi
1 mm/min; ISO 527
2.90 GPa
421 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 108 MPa
15700 psi
2 mm/min; ISO 178
120 MPa
17400 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.45 GPa
355 ksi
2 mm/min; ISO 178
2.60 GPa
377 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.300 J/cm
0.562 ft-lb/in
ASTM D256
0.300 J/cm

@Temperature -30.0 °C
0.562 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*3; ISO 180/1A
4.00 kJ/m²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*3; ISO 180/1U
45.0 kJ/m²

@Temperature -30.0 °C
21.4 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*3 sp=62mm; ISO 179/1eU
4.70 J/cm²

@Temperature -30.0 °C
22.4 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
0.300 J/cm²

@Temperature -30.0 °C
1.43 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 30.0 J

@Temperature 23.0 °C
22.1 ft-lb

@Temperature 73.4 °F
ASTM D3763
Taber Abrasion, mg/1000 Cycles 10
10
CS-17, 1 kg; ASTM D1044
10
10
CS-17, 1 kg; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature -40.0 - 95.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 203 °F
ASTM E 831
70.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
38.9 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature -40.0 - 95.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 203 °F
ASTM E 831
70.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
38.9 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
Specific Heat Capacity 1.40 J/g-°C
0.335 BTU/lb-°F
ASTM C351
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ASTM C177
0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ISO 8302
Hot Ball Pressure Test <= 140 °C
<= 284 °F
IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 131 °C
268 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
133 °C

@Thickness 3.20 mm
271 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 118 °C
244 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
119 °C

@Thickness 3.20 mm
246 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 138 °C
280 °F
Rate B/50; ISO 306
139 °C
282 °F
Rate B/50; ASTM D1525
140 °C
284 °F
Rate B/120; ISO 306
Flammability, UL94 V-2

@Thickness 1.50 mm
V-2

@Thickness 0.0591 in
UL 94 by SABIC-IP
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
UL 94 by SABIC-IP
Optical Properties Metric English Comments
Refractive Index 1.584
1.584
ASTM D542
1.584
1.584
ISO 489
Haze <= 0.80 %

@Thickness 2.54 mm
<= 0.80 %

@Thickness 0.100 in
ASTM D1003
Transmission, Visible 88 %
88 %
2.54 mm; ASTM D1003
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C Passes
IEC 60695-10-2
Erichson scratch depth, 6N 14micrometer
SABIC Method
Pencil Hardness test, 1kgf H
ASTM D3363
Specific Volume 0.85cm^3/g
ASTM D792