- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 147 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 147 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | ASTM D648-95 |
| Multibase Multi-Pro® 4003 R Medium Impact 40% Glass Filled Polypropylene Moisture content is 0.06%. Multi-Pro 4003 R is a glass reinforced polypropylene compound featuring extremely high stiffness and high impact resistance. Suitable for engineering applications and au.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C @Thickness 3.18 mm |
297 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Maxxam™ PPH-40T Nat Polypropylene Homopolymer (PP Homopolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® LGK4010 PC (Asia Pacific) |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL36ELH PC LNP* Lubricomp* DFL36ELH is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated, Low Extractible, Easy Moldi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL36XXJ PC LNP* Lubricomp* DFL36XXJ is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated, Low Extractable, Healthcare.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP Lubricomp DFP22H PC LNP* Lubricomp* DFP22H is a compound based on Polycarbonate containing Glass Fiber and PTFE. Characteristics of this grade are: Internally Lubricated and Healthcare.This data was supplied by SABIC.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL36ELH PC (Asia Pacific) LNP* Lubricomp* DFL36ELH is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP KX06415 Acetal Copolymer LNP LUBRICOMP* KX06415 is a compound based on Acetal Copolymer resin containing 10% PTFE, 10% Aramid Powder. Added features of this material include: Easy Molding, Heat Stabilized, Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP SG004 PA12 (Europe-Africa-Middle East) LNP* LUBRICOMP* SG004 is a compound based on PA 12 resin containing Graphite. Added features include: Internally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON DE003Z PC LNP STAT-KON* DE003Z is a compound based on Polycarbonate resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive, Extrusion Grade. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Stat-kon DEF13 PC LNP* Stat-kon* DEF13 is a compound based on Polycarbonate resin containing Glass Fiber, Glass Fiber, Carbon Fiber. Added features of this material include: Electrically Conductive.This data was sup.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON DX06500 PC (Asia Pacific) LNP* Stat-kon* DX06500 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Thermocomp DF002L PC LNP THERMOCOMP* DF002L is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Low Extractible.This data was supplied by SABIC-IP for the America.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP DF006HL PC LNP THERMOCOMP* DF006HL is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material include: Low Extractible, Healthcare. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP DF006HL PC LNP THERMOCOMP* DF006HL is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material include: Low Extractible, Healthcare. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PC CF10 TL15 FR BK 10% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 10% Filler by WeightAdditive: PTFE LubricantFeatures: Lubricated and Flame RetardantAppearance: BlackInformation provided.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | ISO 75 |
| Teijin Panlite® GN-3410R Improved Mold Release, Glass Fiber Reinforced, Flame Resistant Polycarbonate Resin GF 10% reinforced, flame retardant and mold release grade, meeting UL 94 V-2.Applications:Mechanical, electric and electronic components that need mechanical property e.g., stiffnessPrecision machin.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | ASTM D648 |
| Samyang Trirex® 3030PJ Polycarbonate PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3030PJ is a high viscosity gradeInformation provided by Samyang. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL GFN3 PPE+HIPS (Asia Pacific) PPE+PS blend. 30% Glass reinforced.FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including pump .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | ASTM D648 |
| A. Schulman VOLOY™ 462 Hybrid Reinforced PBT Alloy Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | ASTM D648 |
| A. Schulman VOLOY™ 462 Hybrid Reinforced PBT Alloy Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | DIN 53461 |
| Polyram RamTough PZ300G8 Polycarbonate, 40% Glass Fiber 40% Glass fiber reinforced polycarbonate for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | ASTM D648 |
| E-Polymers TEKANATE™ G710 , 10% Glass Fiber Reinforced Poly Carbonate 10% Glass Fiber reinforcedInformation provided by E-Polymers Co. Ltd. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | |
| Arkema Group Rilsan® BESN P40 W5 TL Nylon 11, Flexible Tubing Grade (Conditioned) Designation ISO 1874-PA11-P,EFHL,22-003Flexible grade for tubes extrusion. Available color: milky white. Light and heat stabilized. Flame retardant agent.Fire-resistant. Flexibility. High impact str.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | ASTM D648 |
| 3M Dyneon™ PVDF 6008/0001 Polyvinylidene Fluoride Polyvinylidene Fluoride (PVDF) is ideal for multiple applications across a wide array of industries. Widely used in the chemical process industry, wire and cable industry, semiconductor industry, an.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | ISO 75 |
| Teijin Panlite® GV-3410R High Flame Retardancy, Glass Fiber Reinforced Polycarbonate Resin GF 10% reinforced, improved flame retardance and mold release grade, meeting UL 94 V-2.Applications:Mechanical, electric and electronic components that need mechanical property e.g., stiffnessPrecis.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP DCP32 PC (Asia Pacific) LNP* Lubricomp* DCP32 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber, Silicone. Added features of this material include: Electrically Conductive, Internally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON MFD03 PP LNP* STAT-KON* MFD03 is a compound based on Polypropylene resin containing 15% Glass Fiber. Added features of this material include: Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON MFD03 PP (Asia Pacific) LNP* Stat-kon* MFD03 is a compound based on Polypropylene resin containing Glass Fiber, Carbon Powder. Added features of this material include: Electrically Conductive. |
|||