SABIC Innovative Plastics LNP LUBRICOMP DFL36ELH PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP DFL36ELH PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* DFL36ELH is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
Physical Properties Metric English Comments
Density 1.55 g/cc
0.0560 lb/in³
ASTM D792
1.55 g/cc
0.0560 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Time 86400 sec
0.0010 - 0.0030 in/in

@Time 24.0 hour
ASTM D955
0.0021 cm/cm

@Time 86400 sec
0.0021 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0060 - 0.0080 cm/cm

@Time 86400 sec
0.0060 - 0.0080 in/in

@Time 24.0 hour
ASTM D955
0.0071 cm/cm

@Time 86400 sec
0.0071 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 112 MPa
16200 psi
ASTM D638
113 MPa
16400 psi
ISO 527
Tensile Strength, Yield 113 MPa
16400 psi
ASTM D638
114 MPa
16500 psi
ISO 527
Elongation at Break 2.5 %
2.5 %
ASTM D638
2.6 %
2.6 %
ISO 527
Elongation at Yield 2.4 %
2.4 %
ASTM D638
2.4 %
2.4 %
ISO 527
Tensile Modulus 9.28 GPa
1350 ksi
1 mm/min; ISO 527
9.65 GPa
1400 ksi
50 mm/min; ASTM D638
Flexural Strength 179 MPa
26000 psi
ASTM D790
180 MPa
26100 psi
ISO 178
Flexural Modulus 8.70 GPa
1260 ksi
ISO 178
8.96 GPa
1300 ksi
ASTM D790
Izod Impact, Notched 1.76 J/cm
3.30 ft-lb/in
ASTM D256
Izod Impact, Unnotched 8.54 J/cm
16.0 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 17.0 kJ/m²
8.09 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 51.0 kJ/m²
24.3 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 21.0 J
15.5 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 7.00 J
5.16 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.57
0.57
ASTM D3702 Modified
Coefficient of Friction, Static 0.49
0.49
ASTM D3702 Modified
K (wear) Factor 54.4 x 10-8 mm³/N-M
27.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 46.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
26.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
47.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
26.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 30.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
16.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
30.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
17.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 149 °C
300 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
147 °C

@Thickness 3.20 mm
297 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 144 °C
291 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
142 °C

@Thickness 3.20 mm
288 °F

@Thickness 0.126 in
unannealed; ASTM D648