Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 189 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	189 °C	372 °F	ASTM D648
NYCOA 5100 HS Heat Stabilized, Impact Modified Nylon 66 Resin NYCOA 5100 HS is an impact modified, heat stabilized Nylon 66 resin used for injection molding. This material is specially formulated to provide improved flexibility and ductility vs standard Nylon ..
Deflection Temperature at 0.46 MPa (66 psi)	189 Â°C	372 Â°F	Edgew 120104 sp=100mm; ISO 75/Be
SABIC Innovative Plastics Ultem ATX203R PEI+PCE 30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 0.46 MPa (66 psi)	189 Â°C	372 Â°F	Edgew 120104 sp=100mm; ISO 75/Be
SABIC Innovative Plastics Ultem ATX203R PEI+PCE (Asia Pacific) 30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific region.
Deflection Temperature at 0.46 MPa (66 psi)	189 Â°C	372 Â°F	Edgew 120104 sp=100mm; ISO 75/Be
SABIC Innovative Plastics Ultem ATX203R PEI+PCE (Europe-Africa-Middle East) 30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Europe-Africa-Middle East regio..
Deflection Temperature at 0.46 MPa (66 psi)	189 Â°C @Thickness 3.20 mm	372 Â°F @Thickness 0.126 in	unannealed; ASTM D 648
SABIC Innovative Plastics ValoxÂ® TS4016 PBT (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region.
Deflection Temperature at 0.46 MPa (66 psi)	189 Â°C @Thickness 3.20 mm	372 Â°F @Thickness 0.126 in	unannealed; ASTM D 648
SABIC Innovative Plastics LNP Thermocomp WB008 PBT LNP* Thermocomp* WB008 is a compound based on Thermoplastic Polyester (PBT) containing Glass Beads.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 0.46 MPa (66 psi)	189 °C @Thickness 3.20 mm	372 °F @Thickness 0.126 in	unannealed; ASTM D 648
SABIC Innovative Plastics LNP Thermocomp TX88477 PU LNP* Thermocomp* TX88447 is a compound based on Polyurethane resin containing proprietary fillers.This data was supplied by SABIC-IP for the Americas region.