- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 243 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 243 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 470 °F | ASTM D648 |
| Quantum Nylon 6/6 MoS2 Filled Information provided by Quantum Advanced Engineering Plastics |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 - 266 °C | 470 - 510 °F | Average value: 251 °C Grade Count:6 |
| Overview of materials for Nylon 66, Mineral Filled, NCG Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Mineral Filled, NCG Fiber Filled". Each property range of values reported is minimum and maxim.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 470 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill FR® PET GF15 FR 15% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 15% Filler by WeightFeatures: Flame RetardantInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-KON RE004MPC PA 66 LNP* STAT-KON* RE004MPC is a compound based on Nylon 66 resin containing 20% Milled Carbon Fiber. Added features of this material are: Exceptional Processing, Clean Compound System, Electrically C.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP RFB71S PA 66 (Europe-Africa-Middle East) LNP* Thermocomp* RFB71S is a compound based on Nylon 66 resin containing Glass Fiber, Glass Bead. Added features of this material include: Heat Stabilized. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 470 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 GF20H 20% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | ASTM D648 |
| A. Schulman ComAlloy® E-16558 30% Glass Fiber Reinforced Nylon Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 470 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 GF20H 20% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | ASTM D648 |
| A. Schulman ComAlloy® E-16558 30% Glass Fiber Reinforced Nylon Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 470 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 GF20H 20% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | ASTM D648 |
| A. Schulman ComAlloy® E-16558 30% Glass Fiber Reinforced Nylon Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | ASTM D648 |
| A. Schulman ComAlloy® E-16558 30% Glass Fiber Reinforced Nylon Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | ASTM D648 |
| A. Schulman ComAlloy® E-16558 30% Glass Fiber Reinforced Nylon Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 470 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 GF20H 20% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | dry; ISO 75-1/-2 |
| DSM EcoPaXX® Q-X07209 PA410-I-GF40 % Glass Reinforced, Impact Modified |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | dry; ISO 75-1/-2 |
| DSM Novamid® 3010GN30 NAT PA66-GF30 FR(17) 30% Glass Reinforced, Flame Retardant |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Rynite® FR530 BK507 Polyethylene Terephthalate (PET)
(Unverified Data**) 30% Glass Reinforced Flame Retardant Polyethylene Terephthalate Rynite FR530 BK507 is a 30% glass reinforced flame retardant modified polyethylene terephthalate resin.Information provided by DuPont .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 470 °F | ASTM D648 |
| Clariant Renol 66G15BL-195 Blue Nylon 66, 15% Glass Fiber Reinforced Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | dry; ISO 75-1/-2 |
| DSM EcoPaXX® Q-HG6 PA410-GF30 30% Glass Reinforced, Heat Stabilized |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | ASTM Test |
| BASF Ultramid® 1310-11 NF2001 PA66 (Dry) Ultramid 1310-11 NF2001 is a controlled crystallization, fast cycling PA6/6 which provides extremely fast cycle times and improved productivity over Ultramid 1000. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | ASTM Test |
| BASF Ultramid® NBX-0025 NF2001 PA66 (Dry) Ultramid NBX-0025 NF2001 is a specialty, unfilled PA6/6. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 446 Glass/Mineral Reinforced, PET Alloy Data provided by the manufacturer, ComAlloy International Company.35% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | ASTM Test |
| BASF Ultramid® 1000-11 NF2001 PA66 (Dry) Ultramid 1000-11 NF2001 is a general purpose nylon 6/6. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | ASTM Test |
| BASF Ultramid® 1000-2 NF2001 PA66 (Dry) Ultramid 1000-2 NF2001 is a general purpose PA6/6. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Rynite® FR530L BK507 Polyethylene Terephthalate (PET) Rynite FR530 BK507 is a 30% glass reinforced flame retardant modified polyethylene terephthalate resin.Information provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Rynite® FR530L NC010 Polyethylene Terephthalate (PET) Rynite FR530 NC010 is a 30% glass reinforced flame retardant modified polyethylene terephthalate resin.Information provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 627 Nylon 6/6, Mineral Reinforced Data provided by the manufacturer, ComAlloy International Company.20% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 470 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® SPS GF40 BK 40% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by WeightFeatures: SyndiotacticAppearance: BlackInformation provided by TP Composites, Inc. |
|||