Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 301 Â°C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	301 Â°C @Thickness 3.20 mm	574 Â°F @Thickness 0.126 in	Annealed; ASTM D648
Solvay Specialty Polymers AmodelÂ® A-1145 HS Polyphthalamide (PPA), 45% Glass Fiber (Dry) AmodelÂ® A-1145 HS is a 45% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, very high flexural modulus and very high tensile strength. Excellent cr..
Deflection Temperature at 0.46 MPa (66 psi)	301 Â°C @Thickness 3.20 mm	574 Â°F @Thickness 0.126 in	Annealed; ASTM D648
Solvay Specialty Polymers AmodelÂ® AS-1145 HS Polyphthalamide (PPA), 45% Glass Fiber (Dry) AmodelÂ® AS-1145 HS is a 45% glass reinforced heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater tha..
Deflection Temperature at 0.46 MPa (66 psi)	301 Â°C	574 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP THERMOCOMP UX04509 PPA LNP* Thermocomp* UX04509 is a compound based on Polyphthalamide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
Deflection Temperature at 0.46 MPa (66 psi)	301 °C	573 °F	Unannealed; ASTM D648
Techmer ES Luriblend® PPA GF30 TL15 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: PTFE Lubricant(15%)Features: Lubricated, Good Wear Resistance, High Heat Resistance and Low ..
Deflection Temperature at 0.46 MPa (66 psi)	301 °C @Thickness 3.18 mm	574 °F @Thickness 0.125 in	Annealed; ASTM D648
Solvay Specialty Polymers Amodel® AS-1145 HS Polyphthalamide (PPA) (Unverified Data**) Amodel AS-1145 HS is a 45% glass reinforced heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater than 0...