- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 417 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 417 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ISO 75 |
| GEHR Plastics PPSU Polyphenylenesulfone Polyphenylenesulfone is an amorphous material, with improved impact and hydrolysis resistance compared to PSU. The usual operating temperature is approximately 180°C. The extremely high notched i.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ISO 75-1,-2 |
| Lanxess Durethan® BKV 115 H2.0 DUS008 000000 Nylon 6, 15% Glass Fiber PA 6, 15% glass fibers, injection molding, impact modified, heat-ageing stabilizedInformation provided by LANXESS. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP IFP36 PA6.12 LNP* LUBRICOMP* IFP36 is a Nylon 6/12 base resin containing 30% Glass Fiber, 15% PTFE/Silicone. Added features of t his grade include: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C @Thickness 3.20 mm |
417 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP IFP36 PA6.12 LNP* LUBRICOMP* IFP36 is a Nylon 6/12 base resin containing 30% Glass Fiber, 15% PTFE/Silicone. Added features of t his grade include: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP Lubricomp JL003 PES LNP* Lubricomp* JL003 is a compound based on Polyethersulfone resin containing PTFE.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C @Thickness 6.40 mm |
417 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM DH1004 PEI |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C @Thickness 6.40 mm |
417 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Ultem DH1004F PEI High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. US FDA and EU Food Contact compliant.This data was supplied by SABIC-IP for the Americas regi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C @Thickness 6.40 mm |
417 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Ultem DH1004F PEI (Asia Pacific) High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. US FDA and EU Food Contact compliant.This data was supplied by SABIC-IP for the Asia Pacific .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C @Thickness 6.40 mm |
417 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Ultem DH1004F PEI (Europe-Africa-Middle East) High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. US FDA and EU Food Contact compliant.This data was supplied by SABIC-IP for the Europe-Africa.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Radel® R-5100 Polyphenylsulfone (PPSU), Filled Radel® R-5100 is an opaque, general purpose polyphenylsulfone (PPSU) for injection molding, that offers exceptional hydrolytic stability, and toughness superior to other commercially-available, h.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-KON EEF42 PEI LNP STAT-KON* EEF42 is a compound based on Polyetherimide resin containing 10% Carbon Fiber, 20% Glass Fiber. Added features of this material include: Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-KON PFD04 PA 6 LNP* STAT-KON* PFD04 is a compound based on Nylon 6 containing 20% Glass Fiber. Added feature of this grade is: Ellectrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-KON PFD04ES PA 6 (Europe-Africa-Middle East) LNP* STATKON* PFD04ES is a compound based on PA 6 resin containing Carbon Powder, Glass Fiber. Added features include: Electrically Conductive, Easy Molding, Heat Stabilized. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-KON PFD04S PA 6 (Europe-Africa-Middle East) LNP* Statkon* PFD04S is a compound based on PA 6 resin containing Glass Fiber, Carbon Powder. Added features include: Electrically Conductive, Heat Stabilized. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C @Thickness 3.20 mm |
417 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP EC005R PEI LNP* THERMOCOMP* EC005R is a compound based on Polyetherimide resin containing 25% Carbon Fiber. Added features include: Mold Release, Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP IF00C PA6.12 LNP* THERMOCOMP* IF00C is a compound based on Nylon 6/12 resin containing 60% Glass Fiber. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C @Thickness 6.40 mm |
417 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Infino® VB-5150GL PBT, 15% Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ASTM D648 |
| Samyang Tramid® 215 Polyamide, High Impact Strong with excellent thermal resistance. Abrasion resistance, chemical resistance and oil resistance are excellent.215 is a high impact grade.Applications:Automotive knob types, door handles and m.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C @Thickness 6.40 mm |
417 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM 9090 PEI (Europe-Africa-Middle East) Polyetherimide Blend with improved Ductility and Detergent resistance. Meets FAR 25.853 and OSU 55/55 heat release and provides low toxicity, smoke and flame evolution. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOTUF PX95726 PA 6 LNP THERMOTUF* PX95726 is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C @Thickness 6.40 mm |
417 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Infino® VB-5150GL PBT, 15% Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ISO 75-1/-2 |
| Unitika A1022GFL15 PA6, 15% Glass Fiber Reinforced, Dry Information provided by Unitika Ltd. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ASTM D648 |
| Westlake Plastics Radel® R Polyphenylsulfone Stock shapes extruded from Radel R resins offer a superior combination of high performance properties that include excellent thermal stability, outstanding toughness and good environmental stress cr.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 612 Nylon 6, Glass Reinforced, UL Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ISO 75 |
| BASF Ultramid® B3GM35 BKQ642 23220 15/25% Glass/Mineral Filled PA6 (Dry) Ultramid B3GM35 BKQ642 23220 is a 40% combined glass-fiber and mineral reinforced, pigmented black injection molding PA6 grade. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ISO 75 |
| BASF Ultradur B 4040 G4 LS High Speed BK15029 20% Glass Filled PBT/PET |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-KON PX05047 PA 6 (Europe-Africa-Middle East) LNP* Stat-kon* PX05047 is a compound based on PA 6 resin containing Carbon Fiber, Proprietary Filler (s). Added features include: Electrically Conductive, High Impact. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C @Thickness 3.20 mm |
417 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP WF002I PBT LNP* THERMOTUF* WF006I is a compound based on PBT resin containing 10% Glass Fiber. Added feature of this grade is: High Impact. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP VERTON PX00700 PA 6 (Asia Pacific) LNP* Verton* PX00700 is a compound based on Nylon 6 resin containing Long Glass Fiber. |
|||