- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 63.0 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 63.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C | 145 °F | ASTM D648 |
| Mytex Polymers AN18KW-01 FK Polypropylene, Rubber modified Description: Rubber modified polypropylene produced for automotive interior applications using Mytex® Technology. Specifically designed to achieve ductile performance at cold temperatures during a.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 63.0 - 67.0 °C | 145 - 153 °F | ASTM D648-06 |
| Proto3000 Objet RGD525 High Temperature Prototyping Polymer Information provided by Proto3000 for their protoyping engineering services. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C | 145 °F | ASTM D648 |
| LyondellBasell Adsylâ„¢ 5C30F Thermoplastic Olefin Resin Primary Processing Method: Film extrusionKey Features: thermoplastic olefin resins for film extrusion, good clarity and gloss, good moisture barrier properties, very low seal initiation temperature,.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C | 145 °F | ASTM D648 |
| LyondellBasell Adsylâ„¢ 5C37F Thermoplastic Olefin Resin Primary Processing Method: Film extrusionKey Features: thermoplastic olefin resins for film extrusion, good clarity and gloss, good moisture barrier properties, very low seal initiation temperature,.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C | 145 °F | ISO 75 |
| LyondellBasell Hifaxâ„¢ CA45 Thermoplastic Olefin Resin Key Features: medium melt flow, medium modulus thermoplastic elastomeric olefin resin, excellent balance of properties, excellent processability, good colorability, excellent surface appearanceAppli.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C @Thickness 3.20 mm |
145 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 330 Ionomer Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C @Thickness 3.20 mm |
145 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 330 Ionomer Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C @Thickness 3.20 mm |
145 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 330 Ionomer Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C @Thickness 3.20 mm |
145 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 330 Ionomer Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C @Thickness 3.20 mm |
145 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 330 Ionomer Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C @Thickness 3.20 mm |
145 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 330 Ionomer Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C | 145 °F | |
| Eastman Ecdel PCCE 9967 Copolyester Ether Elastomer ISO data as provided by the manufacturer, Eastman Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 63.0 - 65.0 °C | 145 - 149 °F | |
| C.O.I.M. EXTER S® S 105 Orthophthalic Resin Description: The Exter S product line contains a large number of unsaturated polyester resin products with an array of properties and applications.Specific Notes for ESTER S® S 105: Medium reactivi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C | 145 °F | ASTM D648 |
| ACC EP QSZ EPI Engineered Polymers Quick Set Epoxy with Zinc EP QSZ Quick Set Epoxy with Zinc, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC’s (Volatile Organic Compound), self-leveling modified epoxy. This versatile new gene.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C | 145 °F | ASTM D648 |
| ACC EP QS EPI Engineered Polymers Quick Set Epoxy EP QS Quick Set Epoxy, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC, self-leveling modified epoxy. This versatile new generation epoxy displays low blush, fast cure.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C | 145 °F | ISO 75-2 |
| Borealis Borsoft™ SG220MO Polypropylene Random Copolymer for Injection Molding Borsoft™ SG220MO is a polypropylene characterized by good flow, high impact and good transparency. This grade contains antistatic and demolding additives which, together with enhanced nucleation, .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 63.0 °C | 145 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP FP003 PE (Europe-Africa-Middle East) LNP *Lubricomp* FP003 is a compound based on Polyethylene resin, containing PTFE and Silicone. Added features include: Internally Lubricated. |
|||