Polymer Property : UL RTI, Mechanical with Impact = 266 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
UL RTI, Mechanical with Impact	75.0 - 130 °C	167 - 266 °F	Average value: 112 °C Grade Count:3
Overview of materials for Polybutylene Terephthalate (PBT), Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Impact Grade". Each property range of values reported is minimum and m..
UL RTI, Mechanical with Impact	125 - 130 °C	257 - 266 °F	Average value: 126 °C Grade Count:4
Overview of materials for Polycarbonate, Gamma Radiation Resistant This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Gamma Radiation Resistant". Each property range of values reported is minimum and maximum..
UL RTI, Mechanical with Impact	80.0 - 130 °C	176 - 266 °F	Average value: 103 °C Grade Count:13
Overview of materials for Polycarbonate, 30% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 30% Glass Filled". Specific grades with glass content between 25% and 34% are included. E..
UL RTI, Mechanical with Impact	75.0 - 130 °C	167 - 266 °F	Average value: 107 °C Grade Count:9
Overview of materials for Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Glass Filled". Each property range of values repor..
UL RTI, Mechanical with Impact	50.0 - 130 °C	122 - 266 °F	Average value: 119 °C Grade Count:3
Overview of materials for Polyimide, Graphite Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyimide, Graphite Filled". Each property range of values reported is minimum and maximum values of app..