- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 129 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 129 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 53.9 °C | 129 °F | ASTM D648 |
| Nylene® 321 (HS) Impact Modified Nylon 6 Description: Nylene® 321 (HS) is an impact modified nylon 6. Information provided by Custom Resins.ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources Corporatio.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | 75/Method Af |
| Premix Thermoplastics PRE-ELEC® PP 1399 Dissipative Thermoplastic Compound PRE-ELEC® PP 1399 is a dissipative thermoplastic compound based on polypropylene. The electrical dissipation is achieved by using special conductive carbon black. In addition to stable surface resi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PP CQX8025 R2 Polypropylene, Mineral Reinforced, Scratch Resistant Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | (from DAM) |
| Ineos ABS Triax® 1180 ABS + Polyamide Blend (Conditioned)
(discontinued **) Key Features:UnfilledHigh impact or high impact modifiedSuitable processing methods:Injection moldingInformation provided by Bayer Polymers.LANXESS was spun-off from Bayer in early 2005. Business r.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 - 136 °C | 129 - 277 °F | Average value: 89.3 °C Grade Count:8 |
| Overview of materials for Thermoset Polyurethane, Liquid This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Polyurethane, Liquid". Each property range of values reported is minimum and maximum values of.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Crastin® S610SF BK851 PBT
(Unverified Data**) Crastin® S610SF is an unreinforced, low viscosity polybutylene terephthalate for injection molding. It has high flow characteristics and is specifically suitable for super fast production.Informati.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75 |
| Phillips Sumika Marlex® CHP-370 Thermoplastic Polyolefin
(discontinued **) Thermoplastic Polyolefin, Good Stiffness and Impact PerformanceApplications: Automotive Pillar TrimConditioning after Molding: 48 hr at 23°CNominal Shrinkage: 0.8-1.0%Drying conditionsTemperature: .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C @Thickness 6.40 mm |
129 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical Lupox® HV1005S PBT Description: Injection Molding, PBT, High ImpactApplication: IT/OA, Automotive (Connector)CAS No. 155123-66-3 and 24968-12-5Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 1-3000 B DEL Polypropylene Homopolymer INNOPOL® CS 1-3000 B DEL is developed for producing injection molded automotive components.All information provided by INNO-COMP. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 1-3000 N DEL Polypropylene Homopolymer INNOPOL® CS 1-3000 N DEL is developed for producing injection molded automotive components.All information provided by INNO-COMP. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP WP004 PBT LNP* LUBRICOMP* WP004 is a compound based on PBT resin containing 20% PTFE/Silicone. Added feature of this grade is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C @Thickness 6.40 mm |
129 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® 312 PBT (Asia Pacific) Unreinforced, For compounding only (not for injection molding), Medium viscosity. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C @Thickness 6.40 mm |
129 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® 315 PBT Unreinforced, For extrusion/compounding only (not for injection molding). High viscosity. Melt viscosity between 7500 and 9500 poise. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C @Thickness 3.20 mm |
129 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® HX215HP PBT High Flow, Unreinforced, Polybutylene Terephthalate (PBT). For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food conta.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C @Thickness 3.20 mm |
129 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® IQ3001 PBT (Europe-Africa-Middle East) Valox IQ3001 is an unfilled environmentally responsible iQ-PBT resin modified with elastomer. Targeted for flexible hinge applications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75-2 |
| Borealis Daplen™ EE158AI Polypropylene TPO Compound Daplen™ EE158AI is a 13% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness, give.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75-2 |
| Borealis Daplen™ EE168AI Polypropylene TPO Compound Daplen™ EE168AI is a 10% mineral filled polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness and is easy to process. .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ASTM D648 |
| Formosa Plastics Formolene® 6507N Impact Copolymer Polypropylene Impact Copolymer for Injection Molding Formolene® 6507N is a medium impact copolymer of polypropylene characterized by its easy mold flow, physical property balance and excellent dimensional stabil.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75 |
| Unipetrol PP MONSTEN® GB 503 Polypropylene Impact Copolymer Made for injection molding applications. Basic stabilization. Impact copolymer.Information provided by Unipetrol RPA |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 53.9 °C | 129 °F | ISO 75-2/A |
| ExxonMobil Exxtral™ BMV 301 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin characterized by a good stiffness/toughness balance, designed for automotive interior application in which good surface finish, high s.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 53.9 °C | 129 °F | ISO 75-2/A |
| ExxonMobil PPU0180F Polypropylene Homopolymer Product Description: An unstabilized homopolymer granular resin designed for automotive and compounding applications.Availability: Europe Processing Method: CompoundingInformation provided by Exxon.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 53.9 °C | 129 °F | |
| Aclo Accutech Polypropylene Copolymer CP0437M20L Mica Reinforced |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ASTM D648 |
| Ashley Polymers Ashlene® 735 Nylon 6 Economy grade, impact modified Nylon 6 for injection molding.Data provided by the manufacturer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ASTM Test |
| BASF Ultramid® B27 E 01 PA6 (Dry) Ultramid B27 E 01 is a low viscosity general-purpose, extrusion PA6 grade well suited for compounding. It conforms to FDA requirements including, 21 CFR 177.1500,EU Directive 2002/72/EC, the German.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75-2 |
| CENTROPLAST CENTROLEN PP-H Polypropylene homopolymer This plastic is a low density, easily machined material that can be welded and has good chemical resistance. Applications include filter housings, chemical pump components and apparatus engineering.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | |
| Ineos ABS Triax® 1180 ABS + Polyamide Blend (DAM)
(discontinued **) Key Features:UnfilledHigh impact or high impact modifiedSuitable processing methods:Injection moldingInformation provided by Bayer Polymers.LANXESS was spun-off from Bayer in early 2005. Business r.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ASTM D648 |
| Albis Plastics Cellulose Acetate Butyrate B900 (Base Grade), 16% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | |
| Isoflon PA 11 Polyamide 11 General use for mechanical partsGood heat resistanceEasy to useInformation provided by Isoflon. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ASTM D648 |
| Adell RZ-16 Copolymer Polypropylene, 30% Calcium Carbonate Filled Data provided by Adell Plastics, Inc. |
|||