| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | |
| Plastcom SLOVALEN PH 78 T 40 PP, 40% mineral filling FeaturesModified homopolymer PP for injection moulding with the content of 40% microground, floated, chemically modified talc. Stable towards detergents. General application in all industry branches.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 3.20 mm |
266 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Cycoloy® C4220K PC+ABS (Asia Pacific) Cycoloy* C4220K resin is an injection moldable 20% glass reinforced non FR PC-ABS.
Key features include improved Knit Line strength, good flow, excellent strength & rigidity, heat resistance & hyd.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| Quadrant EPP Quadrant PC 1000 extruded (ISO Data) Quadrant Engineering Plastic Products is marketing non-UV-stabilized polycarbonate stock shapes under the trade name Quadrant PC 1000. It is a natural, “non-optical” industrial quality (clear, tra.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 - 177 °C | 266 - 351 °F | Average value: 162 °C Grade Count:31 |
| Overview of materials for Nylon 12, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 130 °C @Thickness 6.40 mm |
>= 266 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LUPOY GN1006FL PC, Halogen Free, Flame Retardant, Transparency Description: Injection Molding, PC, Halogen Free Flame Retardant, TransparencyApplication: IT/OA, Electric & Electronic Housing and ComponentsCAS: 103598-77-2Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 130 °C @Thickness 6.40 mm |
>= 266 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LUPOY GN1006FMR PC, Halogen Free, Flame Retardant, Transparency Description: Injection Molding, PC, Halogen Free Flame Retardant, Transparency, Mold ReleaseApplication: IT/OA, Electric & Electronic Housing and ComponentsCAS: 103598-77-2Information provided by LG.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 130 °C | >= 266 °F | ISO 75-2 |
| Menzolit Menzolit® BMC 0180 Unsaturated Polyester UP BMC 0180 is a general purpose BMC for electrical applications. Product according to type 803 DIN 16911. The glass content is on a level that combines good mould ability with good strength and stiffn.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 6.40 mm |
266 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LUPOY HI1002ML PC, High Impact Description: Injection Molding, PC, General Purpose, High Impact, Chemical ResistanceApplication: Mobile Phone HousingCAS: 103598-77-2 and 9046-16-6Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 6.40 mm |
266 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LUPOY SC1004A PC Description: Injection Molding, PC, General Purpose, High Toughness, Chemical resistance, High Impact (at Low Temperature)Application: Mobile Phone HousingCAS: 103598-77-2 and 143106-82-5Information.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| Mitsubishi Xantar® 18 R Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| Mitsubishi Xantar® 18 SR FD Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| Mitsubishi Xantar® 19 R Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| Mitsubishi Xantar® 22 R Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| Mitsubishi Xantar® 22 UR Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| Mitsubishi Xantar® FC 22 R Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| Mitsubishi Xantar® FC 22 UR Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| Mitsubishi Xantar® FC 25 R Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 130 °C @Thickness 6.40 mm |
>= 266 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LUPOY GP1006FL PC, Flame Retardant Description: Injection Molding, PC, Flame Retardant, High FlowApplication: IT/OA, E&E Housing and ComponentsCAS: 103598-77-2Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 130 °C @Thickness 6.40 mm |
>= 266 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LUPOY GP1006FM PC, Flame Retardant Description: Injection Molding, PC, Flame RetardantApplication: IT/OA, E&E Housing and ComponentsCAS: 103598-77-2Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| Mitsubishi Xantar® F 25 UR Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 3.20 mm |
266 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Xenoy® RCX201 PC+PET (Asia Pacific) |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75 |
| Teijin Panlite® LS-2250 Friction and Abrasion Resistant Polycarbonate Resin It is compounded with fluorine powder to improve friction and abrasion resistance, meeting UL 94 V-2. The friction and abrasion resistance is superior than that of polyamidoacetal, maintaining excel.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 6.40 mm |
266 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Infino® TP-1002 PC, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75 |
| Polyram RamTough PZ513 Polycarbonate, Easy Flow, Flame Retardant Transparent polycarbonate, UV stabilized, easy flow, flame retardant, for injection molding applications.Information provided by Polyram. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® XE 4028 nat PA12/MACMI Product description: Grilamid XE 4028 natural is a transparent thermoplastic polyamides based on aliphatic, cycloaliphatic and aromatic blocks. Grilamid XE 4028 natural offers a variety of interesti.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Eurostar Starflam PK0069 PA6, Mineral Fiber Filled, Flame Retardant, Injection Molded Starflam PK0069 is a Free Flame Retardant Mineral Filled Polyamide 6 Injection Molding Resin (also known as Starflam PA6 30E6 Z88)Information provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | 120°C/hr; ASTM D 648 |
| Cossa Polimeri ESTAPROP KUR 1060 GFC Polypropylene, 30% Glass Filled PP copolymer 30% chemically coupled glass fiberElastomer modified, good impact strengthInformation provided by Cossa Polimeri S.r.l. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 130 °C | >= 266 °F | ASTM D648 |
| E-Polymers TEKANATE® G7013FR General Purpose Easy Molding Flame Retardant Polycarbonate Modified Poly Carbonate: TEKANATE is a modified PC by improving polycarbonate resins with features of halogen-free flammability, transparency, impact resistance and reinforced fiberglass. It shows .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | STN EN ISO 75/A |
| Plastcom SLOVALEN PH 79 GF 20 Polypropylene Homopolymer, 20% Glass Fiber FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 20% glass fiber, contains the modifier of mechanical properties. Increased strength in comparison with unfilled PP.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp PK0069 PA 6 (Europe-Africa-Middle East) LNP* THERMOCOMP* PK0069 is a compound based on PA 6 resin containing Glass Bead, Flame Retardant. Added features include Flame Retardant.This data was supplied by SABIC-IP for the Europe-Africa-Midd.. |
|||