- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 192 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 192 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | ISO 75, ASTM D648 |
| Nilit Nilamon B3 H7 GK 35 15% Glass Fiber, 25% Mineral Reinforced PA6 Description: Nilamon B3 H7 GK 35 provides a combination between low warpage and high stiffness, while retaining a good impact strength. It has a high heat aging resistance, so that it is suitable fo.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 377 °F | Unannealed; ASTM D648 |
| Ravago Manufacturing Americas Hylon® N1240MHL BK Nylon 6/6 Available in North America Filler: Mineral, 40% Filler by WeightAdditive: Heat Stabilizer and Lubricant Features: Lubricated, Low Warpage and Heat StabilizedRoHS CompliantForm: Pellets Processing .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C @Thickness 3.20 mm |
378 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP KONDUIT PX08321 PA 6 LNP* Konduit* PX08321 a compound based on PA6 resins containing mineral. Added features include: Thermally Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C @Thickness 3.20 mm |
378 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP KONDUIT PX08321 PA 6 (Asia Pacific) Thermally conductive mineral filled PA6 compound |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | ASTM Data |
| BASF Capron® 8230G HS 6% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron 8230G HS is a heat stabilized, 6% nylon 6 molding compound offering improved stiffness and dimensional stability in thin sections. It exhibits a combination of strength, stiffness and perfor.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | ASTM D648 |
| Kuraray Genestarâ„¢ TA104 Nylon Reinforced injection grade.Main Features:High reflectivityLess color change by heat and lightHigh reliabilityExample of applications:LED reflectors |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Ultem 1010KM PEI (Asia Pacific) Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Ultem 1010KM PEI (Europe-Africa-Middle East) Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Ultem 2312EPR PEI (Europe-Africa-Middle East) 30% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.This data was supplied by SABIC-IP for the Eu.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C @Thickness 3.20 mm |
378 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® IQ4860HR PBT Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C @Thickness 3.20 mm |
378 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® IQ4860HR PBT (Asia Pacific) Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C @Thickness 3.20 mm |
378 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® IQ4860HR PBT (Europe-Africa-Middle East) Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP IX04513C PA 6/12 (Asia Pacific) LNP THERMOCOMP* IX04513C is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Clean Compounding System. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Ultem 1010KM PEI Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP WF004 PBT (Europe-Africa-Middle East) LNP* Thermocomp* WF-1004 is a compound based on Polybutylene Terephalate resin containing Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | ISO 75-1, 2 |
| Polyplastics Duranex® HN7315 Polybutylene Terephthalate (PBT), Low warpage, 15% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | GB-1634 |
| Zhejiang Juner PA-A6-3 GF/MF Reinforced Applications: Shell of Middle & Top Grade MCB, Pedestal & Shell of Low Voltage Electrical ApplianceInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Eurostar Starflam RF023P PA66/6, Glass Fiber Filled, Flame Retardant, Injection Molded Starflam RF0023P is a Flame Retardant, Halogen Free, Red Phosphorous Free, Glass Reinforced Polyamide 66/6 Injection Molding (also known as Starflam PA66C U2 Z23)Information provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | ISO 75 |
| BASF Petra® 110 BK-112 15% Glass Filled PET Petra 110 is a 15% glass fiber reinforced, black pigmented, polyethylene terephthalate injection molding compound. It exhibits a good combination of performance properties including good strength a.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | ASTM D648 |
| Beijing Ranger Chem PBT-201-G10 272 Flame Retarding FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 412 Polyester - PBT, Glass Reinforced Data provided by the manufacturer, ComAlloy International Company.15% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | ISO 75 |
| BASF Ultradur S 4090 G6 LS BK15077 30% Glass Filled PBT |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | ASTM D648 |
| A. Schulman ComAlloy Lubrilon® 646 Nylon 6/12, Carbon Fiber/PTFE Reinforced Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma.. |
|||