- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 350 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 350 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | ASTM D648 |
| Polymer Resources AC-G10 Acetal Copolymer, 10% Glass Reinforced Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | Annealed, 0.125 in bars; ASTM D648 |
| PolyOne Lubri-Tech™ PF-000/15T Polysulfone, PTFE Lubricated
(discontinued **) Description/Features:PTFE LubricatedUL 94 V0PolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | Annealed, 0.125 in bars; ASTM D648 |
| PolyOne Lubri-Tech™ PF-30CF/15T Polysulfone, Carbon Fiber Reinforced, PTFE Lubricated
(discontinued **) Description/Features:Carbon Fiber ReinforcedPTFE LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | |
| Greene Tweed Arlon® 1000 Polyketone Arlon® is a tough, high-temperature, semi-crystalline, thermoplastic presenting a unique combination of mechanical, thermal, chemical and electrical properties. Greene, Tweed uses several proprie.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GB20 L BK 20% Glass Bead Filler Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 20% Filler by WeightAdditive: LubricantFeatures: LubricatedAppearance: BlackInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GB25 L BK 25% Glass Bead Filler Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 25% Filler by WeightAdditive: LubricantFeatures: LubricatedAppearance: BlackInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA11 GF30 TL20 LE 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: Heat Stabilizer and PTFE LubricantFeatures: Good Wear Resistance, Low Extractables, Lubricat.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 AF Nylon 66 Availability: North AmericaForms: PelletsFiller/Reinforcement: Aramid FiberAdditive: Heat Stabilizer and LubricantFeatures: Lubricated, Good Wear Resistance, Low Friction and Heat StabilizedInformat.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 AF10 Nylon 66 Availability: North AmericaForms: PelletsFiller/Reinforcement: Aramid Fiber, 10% Filler by WeightAdditive: LubricantFeatures: Lubricated, Good Wear Resistance and Low FrictionInformation provided by.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GF10 10% Glass Fiber Reinforced PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GF10 10% Glass Fiber Reinforced PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GF10 10% Glass Fiber Reinforced PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GF10 10% Glass Fiber Reinforced PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | |
| TriStar CJ Composite Bearing This family of materials offers the combination of high compressive strength, low coefficient of friction, and excellent abrasion and corrosion resistance while running without lubrication. They are.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | |
| TriStar FCJ Composite Bearing This family of materials offers the combination of high compressive strength, low coefficient of friction, and excellent abrasion and corrosion resistance while running without lubrication. They are.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GF10 10% Glass Fiber Reinforced PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | Unannealed; ASTM D648 |
| PolyOne Edgetek® PF-10GF/000 Polysulfone, Glass Filled
(discontinued **) Description/Features:Glass Fiber ReinforcedUL 94 V0PolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||