- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 61.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 61.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | ASTM D648 |
| Nylene® 733 Nylon 6 Dry as molded. Injection molding grade. Nylene 733 is a high impact modified nylon suitable for both molding and extrusion. Parts molded from 733 have excellent impact strength right out of the mol.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | ASTM D648 |
| North Wood Plastics Polypropylene with 20% Wood Fiber, Molding Grade Data provided by North Wood Plastics, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C @Thickness 3.18 mm |
142 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Maxxam™ DP 9052-3-1000 Polyethylene, High Density (HDPE) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | |
| Polimeri Europa KOBLEND HI 18 PBT+PC, Impact Grade
(discontinued **) Symbol according to ISO 1043/1: PBT+PC-HI Elastomer modified PBT+PC blend, similar to KOBLEND HI 10 with improved impact resistance at low temperatures and better thermal properties. Main applicat.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C @Thickness 6.40 mm |
142 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical Lupox® DP1000DU PBT Description: Injection Molding, PBT, General PurposeCAS No. 30965-26-5Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C @Thickness 6.40 mm |
142 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical Lupox® GP1000A PBT Description: Injection Molding, PBT, General PurposeApplication: Automotive (Head Lamp Bezel)CAS No. 30965-26-5Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C @Thickness 6.40 mm |
142 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical Lupox® GP1000D PBT Description: Injection Molding, PBT, General PurposeApplication: Automotive (Head Lamp Bezel)CAS No. 30965-26-5Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | ISO 75-1,-2 |
| Gromax BTE35-DN00N1 Nylon 6 (Dry) Information provided by Gromax Enterprises Corp. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | ISO 75-1,-2 |
| Gromax BTE70-FN001N1 Nylon 6 (Dry) Information provided by Gromax Enterprises Corp. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C @Thickness 3.20 mm |
142 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP IL004 PA 6/12 (Asia Pacific) LNP* Lubricomp* IL004 is a compound based on Nylon 6/12 resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Lubricomp IP003 PA6.12 LNP* Lubricomp* IP003 is a Nylon 6/12 base resin containing PTFE and Silicone.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| SABIC Innovative Plastics SABIC PPCOMPOUND 7985 PP SABIC® PPcompound 7985 is a mineral filled, impact modified polypropylene TPO. This material combines scratch resistance and heat stability with interior automotive UV stability. The IMDS is 2097.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON MD000I PP (Europe-Africa-Middle East) LNP* Stat-kon* MD000I is a compound based on Polypropylene resin. Added features of this material include: Electrically Conductive, High Impact. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP MX95318 PP LNP* THERMOCOMP* MX95318 is a compound based on Polypropylene containing Proprietary Filler(s). |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP PB006SXS PA 6 (Europe-Africa-Middle East) LNP* THERMOCOMP* PB006SXS is a compound based on PA 6 resin containing Glass Bead. Added features include: Heat Stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp RX06027 PA 66 (Europe-Africa-Middle East) LNP* THERMOCOMP* RX06027 is a compound based on PA 66 containing Glass Bead. Added features include: Easy Molding, Heat Stabilized, UV-Stabilized.This data was supplied by SABIC-IP for the Europe-A.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP IP004Z PA6.12 (Europe-Africa-Middle East) LNP* LUBRICOMP* IP004Z is a compound based on PA 6/12 resin containing PTFE, Silicone. Added features include : Internally Lubricated, Extrusion grade. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP 2X00858 FP-F (FEP) LNP* THERMOCOMP* 2X00858 is a compound based on FEP resin containing proprietary fillers. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp MB008S PP (Asia Pacific) LNP* Thermocomp* MB008S is a compound based on Polypropylene resin containing Glass Bead. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Asia Pa.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP PB006EQ PA 6 (Europe-Africa-Middle East) LNP *THERMOCOMP* PB006EQ is a compound based on PA 6 containing Glass Bead. Added features include Reduced Moisture. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP TF002 PU LNP* THERMOCOMP* TF002 is a compound based on Polyurethane resin containing 10% Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Absolute Drying; ASTM-D648 |
| Toyobo GLAMIDE® NB-1700 Nylon/Olefin GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | ASTM D648 |
| Eastman Aspira EN177 Copolyester Resin for Extrusion Blow Molding Applications:Beverage packagingConsumer packagingFood packagingPersonal care packagingKey Attributes:BPA-freeCompatible with high-output manufacturing platformsExcellent clarityHigh gloss appearance.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | ASTM D648 |
| Eastman Eastar EN067 Copolyester, Natural Eastar Copolyester EN067 is a copolymer PET with good color. This product is supplied as a crystalline pellet that has improved flowability characteristics. Due to slower crystallization kinetics, t.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | ASTM D648 |
| Eastman Tenite 285A2R30018 Cellulose Acetate Butyrate, Natural, Trsp Applications:OphthalmicsOptical safety framesProduct Description: Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, cla.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® ST801AHS BK010 Nylon 66
(Unverified Data**) Super Toughened Heat Stabilized Polyamide 66 Zytel ST801AHS BK010 is a Super Tough high performance black polyamide 66 resin. It offers outstanding molding performance in injection molding applicati.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | ISO 75-2/AF |
| Addiplast Addilene H 490 S Flame Retardant Polypropylene Flame retardant, unreinforced, with halogensInformation provided by Addiplast. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | ISO 75-2/AF |
| Addiplast Addilene J 490 M20S Flame Retardant Polypropylene, 20% Mineral Filled Flame retardant, mineral filled, with halogensInformation provided by Addiplast. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Unannealed |
| Aardvark Polymers Aardalloy® 3326 POM Alloy Rotational Molding Resin Aardalloy 3326 is an acetal alloy formulated for enhanced impact resistance and elongation.Aardalloy 3326 maintains the high degree of chemical resistance and low fuel permeation rates of unfilled a.. |
|||