- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 73.9 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 73.9 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D-648 |
| Plaskolite Optix® CA - 51 HF UVT General Purpose Acrylic Resin OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C @Thickness 3.18 mm |
165 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Geon™ Vinyl Rigid Extrusion L0659 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Nilit Polynil® P200 High Viscosity Nylon 66 Description: High viscosityApplication: Semi-finished and FilmInformation provided by NILIT. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Polymer Resources NY6-GP2 General Purpose Nylon 6, Nucleated General Purpose Nylon 6, Nucleated Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C @Thickness 3.18 mm |
165 °F @Thickness 0.125 in |
Compression Molded, annealed at 50 deg.C; ASTM D648 |
| PolyOne Geon™ Vinyl Dry Blend E1501 Polyvinyl Chloride, Rigid (PVC, Rigid) VSI FLAMMABILITY:Burn Length (0.040 in Bar)ASTM D635 0* IN.Burn Time (0.040 in Bar) ASTM D635 0* Sec.*Extinguished before 25 MM starting ref mark.Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C @Thickness 3.18 mm |
165 °F @Thickness 0.125 in |
Compression Molded, Annealed at 50 deg.C; ASTM D648 |
| PolyOne Geon™ Vinyl Dry Blend E6950 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C @Thickness 3.18 mm |
165 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Geon™ Vinyl Dry Blend E7364 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Polymer Resources NY66-IM1-[color]H Nylon, Medium Impact Modified, Heat Stabilized (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 - 220 °C | 165 - 428 °F | Average value: 131 °C Grade Count:15 |
| Overview of materials for Nylon 66, Mineral Filled, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Mineral Filled, Impact Grade". Each property range of values reported is minimum and maximum v.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Fiberfil® PP-60/CC/40 Polypropylene Homopolymer, 40% Calcium Carbonate Information provided by FIBERFIL Engineered Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Fiberfil® PP-60/VO/NH Polypropylene Homopolymer, Flame Retardant, non-halogenated, UL94 V0 Information provided by FIBERFIL Engineered Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | Unannealed (0.250"); ASTM D648 |
| LTL Color Compounds ColorFast® FRA202 General Purpose ABS General purpose V0/5VA-rated ABSAll information provided by LTL Color Compounders, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | Unannealed (0.250"); ASTM D648 |
| LTL Color Compounds ColorFast® FRA204 ABS High gloss, excellent impact ABS, V0/5VA-ratedAll information provided by LTL Color Compounders, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Fiberfil® PP-60/CC/30 Polypropylene Homopolymer, 30% Calcium Carbonate Information provided by FIBERFIL Engineered Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® HIPS 484 GY Availability: North AmericaForms: PelletsAppearance: GreyInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Spartech Royalite R722 PVC Alloy Aircraft Grade Sheet Description: Aircraft Grade SheetInformation provided by Spartech. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Spartech Royalite R87/59 ABS/PVC Weather Resistant Sheet Description: Weather Resistant SheetInformation provided by Spartech. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | Unannealed; ASTM D648 |
| Techmer ES Plastiblend® PA6/6 HS L N Nylon 66 Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier and Nucleating AgentFeatures: Heat Stabilized, Impact Modified and NucleatedProcessing Method: Injection MoldingIn.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | Unannealed; ASTM D648 |
| Techmer ES Plastiblend® PC/ABS FR 6206 Availability: North AmericaForms: PelletsFeatures: Flame RetardantInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill FR® PP FR-N X BKN001 Availability: North AmericaForms: PelletsFeatures: Flame Retardant Appearance: BlackInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6 0254 B Barium Sulfate Filler Availability: North AmericaForms: PelletsFiller/Reinforcement: Barium SulfateFeatures: High Specific GravityInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| A. Schulman SCHULAMID® 6 GB30 30% Glass Bead Reinforced Nylon 6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| A. Schulman SCHULAMID® 6 GB30 30% Glass Bead Reinforced Nylon 6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Westlake Plastics HIPS High Impact Polystyrene HIPS is a low cost plastic material that is easy to machine and fabricate. It is often specified for low strength structural applications when impact resistance, machinability, and low cost are req.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Colorite Polymers 2010 Rigid PVC Description: Colorite Polymers offers a wide range of rigid vinyl compounds for extrusion and injection molding applications for the medical industry. These compounds can be formulated for the produ.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | |
| Aclo Accutech Polypropylene Homopolymer HP0334M30CL Mica Reinforced Coupled |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | |