Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 428 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	193 - 220 °C	379 - 428 °F	Average value: 210 °C Grade Count:29
Overview of materials for Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled". Specific grades with glass content between 45..
Deflection Temperature at 1.8 MPa (264 psi)	73.9 - 220 °C	165 - 428 °F	Average value: 131 °C Grade Count:15
Overview of materials for Nylon 66, Mineral Filled, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Mineral Filled, Impact Grade". Each property range of values reported is minimum and maximum v..
Deflection Temperature at 1.8 MPa (264 psi)	200 - 220 °C	392 - 428 °F	ISO 75 A
Vyncolit G885 Novolac Phenolic Glass fiber and mineral filled phenolic molding compound with excellent mechanical and thermal properties. Information provided by Vyncolit, a Sumitomo Bak Group
Deflection Temperature at 1.8 MPa (264 psi)	90.0 - 220 °C	194 - 428 °F	Average value: 128 °C Grade Count:7
Overview of materials for Nylon 66/6, Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, Mineral Reinforced". Each property range of values reported is minimum and maximum values of..
Deflection Temperature at 1.8 MPa (264 psi)	204 - 220 °C	399 - 428 °F	Average value: 211 °C Grade Count:26
Overview of materials for Polyethersulfone (PES), 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 20% Glass Fiber Filled". Each property range of values reported is minimum and m..
Deflection Temperature at 1.8 MPa (264 psi)	204 - 220 °C	400 - 428 °F	Average value: 214 °C Grade Count:22
Overview of materials for Polyethersulfone (PES), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% ..
Deflection Temperature at 1.8 MPa (264 psi)	65.6 - 220 °C	150 - 428 °F	Average value: 191 °C Grade Count:49
Overview of materials for Polybutylene Terephthalate (PBT), Glass + Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Glass + Mineral Filled". Each property range of values reported is min..