Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 1.50 - 80.0 µm/m-°C | 0.833 - 44.4 µin/in-°F | Average value: 23.9 µm/m-°C Grade Count:23 |
Overview of materials for Nylon 66/6, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are incl.. |
|||
CTE, linear | 1.50 µm/m-°C | 0.833 µin/in-°F | at Set Pt. |
Ferro EG 0225 Specialty Glass Glass Type: MG-Al-Si (devitrified) Typical Powder Form: MVG, SRRG Typical Application: Sintering Aid / Ceramic Ferro offers a wide range of compositions for specialty applications including sinteri.. |
|||
CTE, linear | 1.50 - 1.80 µm/m-°C | 0.833 - 1.00 µin/in-°F | |
MarkeTech H-2 Honeycomb Ceramic MarkeTech International special honeycomb ceramics have a uniform lattice structure, low expansion coefficient, good thermal shock resistance, higher specific surface area, low-pressure drop, and lo.. |
|||
CTE, linear | 1.50 - 1.80 µm/m-°C | 0.833 - 1.00 µin/in-°F | |
MarkeTech H-3 Honeycomb Ceramic MarkeTech International special honeycomb ceramics have a uniform lattice structure, low expansion coefficient, good thermal shock resistance, higher specific surface area, low-pressure drop, and lo.. |
|||
CTE, linear | 1.50 - 1.80 µm/m-°C | 0.833 - 1.00 µin/in-°F | |
MarkeTech H-4 Honeycomb Ceramic MarkeTech International special honeycomb ceramics have a uniform lattice structure, low expansion coefficient, good thermal shock resistance, higher specific surface area, low-pressure drop, and lo.. |
|||
CTE, linear | 1.50 µm/m-°C @Temperature 0.000 - 70.0 °C |
0.833 µin/in-°F @Temperature 32.0 - 158 °F |
DIN 53752 |
Borealis Beta-PPR™ RA7050 Polypropylene-Random-Copolymer for Pressure Pipe Systems Beta-PPR RA7050 is a PP-RCT, a Polypropylene-Random-Copolymer with an enhanced Crystalline structure brought about by a special ß-nucleation and with an improved Temperature resistance. Proof of t.. |
|||
CTE, linear | 1.50 µm/m-°C @Temperature 0.000 - 70.0 °C |
0.833 µin/in-°F @Temperature 32.0 - 158 °F |
DIN 53752 |
Borealis Beta-PPR™ RA7050-GN Polypropylene-Random-Copolymer for Pressure Pipe Systems Beta-PPR RA7050-GN is a PP-RCT, a Polypropylene-Random-Copolymer with an enhanced Crystalline structure brought about by a special ß-nucleation and with an improved Temperature resistance. Proof o.. |
|||
CTE, linear | 1.50 µm/m-°C | 0.833 µin/in-°F | Cured |
Atom Adhesives AA-DUCT 902 Epoxy Adhesive and Coating AA-DUCT 902 is an epoxy adhesive and coating formulation based on pure silver. This versatile silver formulation offers the maximum continuity of conductivity with an electrical resistivity value of.. |
|||
CTE, linear | 1.50 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
0.833 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ISO 11359-2 |
Ascend Performance Materials Vydyne® R633 Nylon 66 Copolymer, 33% Glass Filled, Dry as Molded Vydyne® R633 is 33% glass-fiber reinforced, PA66/6 copolymer resin for superior surface appearance. Available in natural, this injection-molding grade resin is lubricated for machine feed and mold .. |
|||
CTE, linear | 1.50 - 198 µm/m-°C | 0.833 - 110 µin/in-°F | Average value: 106 µm/m-°C Grade Count:14 |
Overview of materials for Polypropylene, Extrusion Grade This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Extrusion Grade". Each property range of values reported is minimum and maximum values of.. |