Polymer Property : CTE, linear = 8.90 Âµin/in-Â°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English
CTE, linear	16.0 Âµm/m-Â°C @Temperature 21.1 - 102 Â°C	8.90 Âµin/in-Â°F @Temperature 70.0 - 215 Â°F
Materion ToughMetÂ® T3 AT110 (OD≥4") ToughMetÂ® is Brush Wellman's solution for severe service material problems. By applying their EquaCastÂ® process, tailored alloying additions and spinodal hardening technology, they have e..
CTE, linear	16.0 Âµm/m-Â°C @Temperature 21.1 - 102 Â°C	8.90 Âµin/in-Â°F @Temperature 70.0 - 215 Â°F
Materion ToughMetÂ® T3 AT120 (OD≥4") ToughMetÂ® is Brush Wellman's solution for severe service material problems. By applying their EquaCastÂ® process, tailored alloying additions and spinodal hardening technology, they have e..
CTE, linear	16.0 Âµm/m-Â°C @Temperature 21.1 - 102 Â°C	8.90 Âµin/in-Â°F @Temperature 70.0 - 215 Â°F
Materion ToughMetÂ® T3 AT120 (OD ToughMetÂ® is Brush Wellman's solution for severe service material problems. By applying their EquaCastÂ® process, tailored alloying additions and spinodal hardening technology, they have e..
CTE, linear	16.0 Âµm/m-Â°C @Temperature 21.1 - 102 Â°C	8.90 Âµin/in-Â°F @Temperature 70.0 - 215 Â°F
Materion ToughMetÂ® T3 AT90 (OD≥4") ToughMetÂ® is Brush Wellman's solution for severe service material problems. By applying their EquaCastÂ® process, tailored alloying additions and spinodal hardening technology, they have e..
CTE, linear	16.0 Âµm/m-Â°C @Temperature 20.0 Â°C	8.90 Âµin/in-Â°F @Temperature 68.0 Â°F
SGL Carbon Group RiduridÂ® V 1640 High Performance Graphite Filled Plastic Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and..
CTE, linear	16.0 µm/m-°C @Temperature 20.0 - 649 °C	8.90 µin/in-°F @Temperature 68.0 - 1200 °F
Eagle Brass 200/201 Nickel Alloy, 1/2 Hardened Nickel 200/201 has properties that are useful in industries such as chemical processing and electronics. Nickel is resistant to various reducing chemicals and alkaline materials. Compared with nick..
CTE, linear	16.0 µm/m-°C @Temperature 20.0 - 649 °C	8.90 µin/in-°F @Temperature 68.0 - 1200 °F
Eagle Brass 200/201 Nickel Alloy, 1/4 Hardened Nickel 200/201 has properties that are useful in industries such as chemical processing and electronics. Nickel is resistant to various reducing chemicals and alkaline materials. Compared with nick..
CTE, linear	16.0 µm/m-°C @Temperature 20.0 - 649 °C	8.90 µin/in-°F @Temperature 68.0 - 1200 °F
Eagle Brass 200/201 Nickel Alloy, 1/8 Hardened Nickel 200/201 has properties that are useful in industries such as chemical processing and electronics. Nickel is resistant to various reducing chemicals and alkaline materials. Compared with nick..
CTE, linear	16.0 µm/m-°C @Temperature 20.0 - 649 °C	8.90 µin/in-°F @Temperature 68.0 - 1200 °F
Eagle Brass 200/201 Nickel Alloy, 3/4 Hardened Nickel 200/201 has properties that are useful in industries such as chemical processing and electronics. Nickel is resistant to various reducing chemicals and alkaline materials. Compared with nick..
CTE, linear	16.0 µm/m-°C @Temperature 20.0 - 649 °C	8.90 µin/in-°F @Temperature 68.0 - 1200 °F
Eagle Brass 200/201 Nickel Alloy, Annealed Nickel 200/201 has properties that are useful in industries such as chemical processing and electronics. Nickel is resistant to various reducing chemicals and alkaline materials. Compared with nick..
CTE, linear	16.0 µm/m-°C @Temperature 20.0 - 649 °C	8.90 µin/in-°F @Temperature 68.0 - 1200 °F
Eagle Brass 200/201 Nickel Alloy, Full Hardened Nickel 200/201 has properties that are useful in industries such as chemical processing and electronics. Nickel is resistant to various reducing chemicals and alkaline materials. Compared with nick..
CTE, linear	16.0 µm/m-°C @Temperature 21.1 - 102 °C	8.90 µin/in-°F @Temperature 70.0 - 215 °F
Materion ToughMet® T3 AT110 (OD ToughMet® is Brush Wellman's solution for severe service material problems. By applying their EquaCast® process, tailored alloying additions and spinodal hardening technology, they have engin..
CTE, linear	16.0 µm/m-°C @Temperature 21.1 - 102 °C	8.90 µin/in-°F @Temperature 70.0 - 215 °F
Materion ToughMet® T3 AT90 (OD ToughMet® is Brush Wellman's solution for severe service material problems. By applying their EquaCast® process, tailored alloying additions and spinodal hardening technology, they have engin..