Polymer Property : Maximum Service Temperature, Air = 370 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	370 °C	698 °F	50% tensile strength reduction at 220 hours
Daelim H&L Plavis-G15 CM 15% Graphite Filled Aromatic Polyimide Bearing Compression Molded. Plavis-G-15: Graphite 15 wt% filled, Self lubricating grade for wear and friction applications.General Plavis information for all grades:PLAVIS polyimide has nitrogen bonded to..
Maximum Service Temperature, Air	370 °C	698 °F	50% tensile strength reduction at 220 hours
Daelim H&L Plavis-G15 DF 15% Graphite Filled Aromatic Polyimide Bearing Direct Formed. Plavis-G-15: Graphite 15 wt% filled, Self lubricating grade for wear and friction applications.General Plavis information for all grades:PLAVIS polyimide has nitrogen bonded to 3 ca..
Maximum Service Temperature, Air	370 °C	698 °F	50% tensile strength reduction at 220 hours
Daelim H&L Plavis-G15 ISO 15% Graphite Filled Aromatic Polyimide Bearing Isostatically Molded. Plavis-G-15: Graphite 15 wt% filled, Self lubricating grade for wear and friction applications.General Plavis information for all grades:PLAVIS polyimide has nitrogen bonded ..
Maximum Service Temperature, Air	370 °C	698 °F	50% tensile strength reduction at 360 hours
Daelim H&L Plavis-G40 CM 40% Graphite Filled Aromatic Polyimide Bearing Compression Molded. Plavis-G-40: Graphite 40 wt% filled, Self lubricating grade with low thermal expansion.General Plavis information for all grades:PLAVIS polyimide has nitrogen bonded to 3 carbo..
Maximum Service Temperature, Air	370 °C	698 °F	50% tensile strength reduction at 360 hours
Daelim H&L Plavis-G40 DF 40% Graphite Filled Aromatic Polyimide Bearing Direct Formed. Plavis-G-40: Graphite 40 wt% filled, Self lubricating grade with low thermal expansion.General Plavis information for all grades:PLAVIS polyimide has nitrogen bonded to 3 carbons is..
Maximum Service Temperature, Air	370 °C	698 °F	50% tensile strength reduction at 360 hours
Daelim H&L Plavis-G40 ISO 40% Graphite Filled Aromatic Polyimide Bearing Isostatically Molded. Plavis-G-40: Graphite 40 wt% filled, Self lubricating grade with low thermal expansion.General Plavis information for all grades:PLAVIS polyimide has nitrogen bonded to 3 car..
Maximum Service Temperature, Air	370 °C	698 °F	50% tensile strength reduction at 200 hours
Daelim H&L Plavis-N CM Unfilled Aromatic Polyimide Bearing Compression Molded. Plavis-N: Best physical properties, maximum electrical and thermal insulation, low out-gassing, superior radiation resistance.General Plavis information for all grades:PLAVIS po..
Maximum Service Temperature, Air	370 °C	698 °F	50% tensile strength reduction at 200 hours
Daelim H&L Plavis-N DF Unfilled Aromatic Polyimide Bearing Direct Formed. Plavis-N: Best physical properties, maximum electrical and thermal insulation, low out-gassing, superior radiation resistance.General Plavis information for all grades:PLAVIS polyimi..
Maximum Service Temperature, Air	370 °C	698 °F	50% tensile strength reduction at 200 hours
Daelim H&L Plavis-N ISO Unfilled Aromatic Polyimide Bearing Isostatically Molded. Plavis-N: Best physical properties, maximum electrical and thermal insulation, low out-gassing, superior radiation resistance.General Plavis information for all grades:PLAVIS ..