- Polymer Property : Thermal Conductivity = 139 BTU-in/hr-ft²-°F
Polymer Property : Thermal Conductivity = 139 BTU-in/hr-ft²-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes Multimet® alloy, 1.32 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 1185°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 600 °C |
139 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 15% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 30% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 40% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes Multimet® alloy, GTAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes Multimet® alloy, GTAW, 6.35 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 600 °C |
139 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes Multimet® alloy, SMAW, 12.7 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 593 °C |
139 BTU-in/hr-ft²-°F @Temperature 1100 °F |
|
| Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 593 °C |
139 BTU-in/hr-ft²-°F @Temperature 1100 °F |
|
| Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 593 °C |
139 BTU-in/hr-ft²-°F @Temperature 1100 °F |
|
| Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 600 °C |
139 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes Multimet® alloy, SMAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 20.0 °C |
139 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
hardened to 62 HRC |
| Bohler-Uddeholm AISI D2 Cold Work Tool Steel AISI D2 is a high-carbon, high-chromium tool steel alloyed with molybdenum and vanadiumAISI AD2 is characterized by: High wear resistance High compressive strength Good through-hardening properties.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 199 °C |
139 BTU-in/hr-ft²-°F @Temperature 390 °F |
hardened to 52 HRC |
| Bohler-Uddeholm POLMAX® 420 Modified - Stainless Mold Steel Polmax is an excellent choice for extreme surface finish requirements. This high performance grade achieves surface finishes that go well beyond conventional tool steels. Polmax is specifically eng.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Assab Steels ASSAB 88 Cold Work Steel ASSAB 88 (SLEIPNER) is a chromium-molybdenum-vanadium alloyed tool steel which is characterized by:Good wear resistanceGood chipping resistanceHigh compressive strengthHigh hardness (>60HRC) after h.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 20.0 °C |
139 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
|
| Assab Steels ASSAB XW-42 Cold Work Steel XW-42 is a high-carbon, high chromium tool steel alloyed with molybdenum and vanadium characterized by:High wear resistanceHigh compressive strength High hardness after hardeningGood through-hardeni.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes Multimet® alloy, 12.7-50.8 mm hot-rolled bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes Multimet® alloy, 533.4 by 82.55 mm forging, stress relieved at 649°C (1200°F), air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||