- Polymer Property : Thermal Conductivity = 20.0 W/m-K
Polymer Property : Thermal Conductivity = 20.0 W/m-K Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 20.0 W/m-K @Temperature 600 °C |
139 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes Multimet® alloy, 1.32 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes Multimet® alloy, 12.7 mm (1/2 in.) thick plate, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 1185°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 15% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 600 °C |
139 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 40% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 600 °C |
139 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes Multimet® alloy, investment-cast, as-cast Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 600 °C |
139 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes Multimet® alloy, SMAW, 12.7 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 593 °C |
139 BTU-in/hr-ft²-°F @Temperature 1100 °F |
|
| Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 593 °C |
139 BTU-in/hr-ft²-°F @Temperature 1100 °F |
|
| Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 35% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes Multimet® alloy, SMAW, 9.5 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Assab Steels ASSAB 88 Cold Work Steel ASSAB 88 (SLEIPNER) is a chromium-molybdenum-vanadium alloyed tool steel which is characterized by:Good wear resistanceGood chipping resistanceHigh compressive strengthHigh hardness (>60HRC) after h.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 200 °C |
139 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 10% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| Thermal Conductivity | 20.0 W/m-K @Temperature 600 °C |
139 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 20% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||