Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 36.0 W/m-K @Temperature 20.0 °C |
250 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
|
Latrobe LSSâ„¢ 2714 Hot Work Tool Steel (DIN 1.2714 mod) TLS 2714 is a nickel-chromium-molybdenum hot work steel that exhibits high impact toughness and good resistance to softening at elevated temperature. The high nickel content imparts the toughness as.. |
|||
Thermal Conductivity | 36.0 W/m-K @Temperature 20.0 °C |
250 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
|
Latrobe LSSâ„¢ 2714T Hot Work Tool Steel (DIN 1.2714 mod) TLS 2714HT is the same steel available from inventory in a heat-treated condition, at a hardness of 352 to 401 HBS (approximately 38 to 43 HRC). TLS 2714HT can be readily flame cut, and this propert.. |
|||
Thermal Conductivity | 36.0 W/m-K @Temperature 20.0 °C |
250 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
|
Zircar Ceramics Alumina Furnaceware ZIRCAR Ceramics Alumina Furnaceware are high purity fully dense, fine grain aluminum oxide products suitable for use in applications with temperatures as high as 1800°C. Such uses include crucibles.. |
|||
Thermal Conductivity | 36.0 W/m-K @Temperature 20.0 °C |
250 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
hardness of 40 HRC |
Bohler-Uddeholm UDDEHOLM ALVAR 14 Hot Work Tool Steel Alvar 14 is a chromium-nickel-molybdenumvanadium alloyed steel ALVAR 14 is characterized by: Good toughnessGood resistance to high thermal stresses Good stability in hardeningGood through-hardening.. |
|||
Thermal Conductivity | 36.0 W/m-K @Temperature 100 °C |
250 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
ATI Allegheny Ludlum AL 304DA Stainless/Carbon Steel Three-Ply Composite Composition above represents only the Type 304 cladding. Its iron content calculated as balance.Allegheny Ludlum AL 304DA is tri-ply composite consisting of a dual stabilized, low carbon steel cent.. |