Processing Properties | Metric | English | Comments |
---|---|---|---|
Processing Temperature | 170 - 180 °C | 338 - 356 °F | Mixture Zone |
Petroquimica Triunfo Trithene® TS 4016 LDPE and LLDPE Blend - Film The Trithene® TS 4016 resin is a mixture of low-density polyethylene (LDPE) with linear low-density polyethylene (LLDPE) designed to meet the needs of the technical films segment for the use of aut.. |
|||
Processing Temperature | 170 - 180 °C | 338 - 356 °F | Collar Temperature |
Solvay Specialty Polymers Cogegum® AFR/930 Polyolefin, Unspecified
(discontinued **) Cogegum® HFFR -Halogen Free Fire Retardant compound Polyolefin based thermoplastic compound containing a fire retardant system that contributes to give the cable self-extinguish properties without .. |
|||
Processing Temperature | 150 - 180 °C | 302 - 356 °F | Average value: 166 °C Grade Count:5 |
Overview of materials for Phenolic/Rubber; Molded This property data is a summary of similar materials in the MatWeb database for the category "Phenolic/Rubber; Molded". Each property range of values reported is minimum and maximum values of approp.. |
|||
Processing Temperature | 170 - 180 °C | 338 - 356 °F | Hardening Temperature |
Möller Medical PolySkin 95 NanoCoating Flexible, very non-abrasive, chemical-resistant decorative coating with easy-to-clean propertiesInformation provided by Möller Medical, Member of CENTROTEC Group |
|||
Processing Temperature | 150 - 180 °C | 302 - 356 °F | Profiles |
Lucobit Lucofin® 1410 Polyolefin TPO Granules, Grey Lucofin is a colored, highly stabilized, bitumen-free TPO raw material based on polyolefins. Lucofin products display excellent tear resistance, flexibility, and weathering resistance. Lucofin exhi.. |
|||
Processing Temperature | 160 - 180 °C | 320 - 356 °F | Membranes |
Lucobit Lucofin® 1411-t1 Polyolefin TPO Granules, White Lucofin are colored, highly stabilized polyolefin-based TPO granules. The t1 series is distinguished by good tenacity, high biaxial extensibility and flexibility outstanding breaking strength, and .. |
|||
Processing Temperature | 160 - 180 °C | 320 - 356 °F | Mold temperature |
Sumitomo Bakelite North America 775 CAF Mineral Filled Diallyl Phthalate Ortho Resin Isomer (DAP). Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Information provided by Sumitomo Bak North Americ.. |
|||
Processing Temperature | 160 - 180 °C | 320 - 356 °F | Mold temperature |
Sumitomo Bakelite North America RX® 3-1-525F-P Short-Glass Reinforced Diallyl Phthalate Ortho Resin Isomer (DAP). Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Meets the requirements of ASTM D5948 Type SDG-F.I.. |
|||
Processing Temperature | 160 - 180 °C | 320 - 356 °F | Mold temperature |
Sumitomo Bakelite North America RX® 3-2-520F-P Short-Glass Reinforced Diallyl Phthalate Isophthalate DAP Resin Isomer. Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Meets the requirements of ASTM D5948 Type SI.. |
|||
Processing Temperature | 160 - 180 °C | 320 - 356 °F | Mold temperature |
Sumitomo Bakelite North America 52-40-40-P Long-Glass Reinforced Diallyl Phthalate Ortho Resin Isomer (DAP). Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Meets the requirements of ASTM D5948 Type GDI-30F.. |
|||
Processing Temperature | 150 - 180 °C | 302 - 356 °F | |
Total EVA 1010 VN 3 Ethylene Vinyl Acetate Copolymer - Blown Film EVA 1010 VN 3 is made by a high pressure tubular process. Grade for films with high transparency and high mechanical properties. Contains an antioxidant.Application examples: Stretch film, food pa.. |
|||
Processing Temperature | 100 - 180 °C | 212 - 356 °F | extruder |
Fainplast Compounds Hax™ HFC 0108/4 Flame Retardant Polyolefin Cable Compound Thermoplastic halogen free flame retardant compound based on polyolefins and mineral fillersGrade description:Bedding, designed to meet BS 7846Information provided by Fainplast Compounds |
|||
Processing Temperature | 100 - 180 °C | 212 - 356 °F | extruder |
Fainplast Compounds Hax™ HF 018/25 Flame Retardant Polyolefin Cable Compound Thermoplastic halogen free flame retardant compound based on polyolefins and mineral fillersGrade description:Insulation; very low thicknessInformation provided by Fainplast Compounds |
|||
Processing Temperature | 100 - 180 °C | 212 - 356 °F | extruder |
Fainplast Compounds Hax™ HF 223F Flame Retardant Polyolefin Cable Compound Thermoplastic halogen free flame retardant compound based on polyolefins and mineral fillersGrade description:High flexibility, good stress crack resistanceInformation provided by Fainplast Compound.. |
|||
Processing Temperature | 150 - 180 °C | 302 - 356 °F | Profiles |
Lucobit Lucobit® 1218 Ethylene Copolymer Bitumen Lucobit® combines the positive properties of polyolefins and bitumen. The material is black and consists of mixtures based on high quality polyethylene copolymers with varying additions of special.. |
|||
Processing Temperature | 160 - 180 °C | 320 - 356 °F | Membranes |
Lucobit Lucofin® 1412-t1 Polyolefin TPO Granules, Light Grey Lucofin are colored, highly stabilized polyolefin-based TPO granules. The t1 series is distinguished by good tenacity, high biaxial extensibility and flexibility outstanding breaking strength, and .. |