- Polymer Property : Cure Time = 4.00 min
Polymer Property : Cure Time = 4.00 min Product List
Processing PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 4.00 - 6.00 min | 0.0667 - 0.100 hour | handling time |
| Permabond ET500 Epoxy Resin PERMABOND ET500 is a two-part fast-setting epoxy adhesive which bonds to a wide variety of substrates such as wood, metal, ceramics and some plastics and composites. It cures rapidly at room tempera.. |
|||
| Cure Time | 4.00 min @Temperature 177 °C |
0.0667 hour @Temperature 350 °F |
|
| TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 350ºF Cure Temperature Millathane® 76 is a very suitable choice for use in products such as bushings, small copier rolls; automotive applications — bumpers, o-rings, hydraulic seals, belts, gaskets, solid tires — and m.. |
|||
| Cure Time | 4.00 - 7.00 min | 0.0667 - 0.117 hour | Working time |
| ITW Devcon 5 minute® Epoxy Gel, Opaque Information provided by ITW Devcon |
|||
| Cure Time | 4.00 - 8.00 min | 0.0667 - 0.133 hour | Working time |
| ITW Devcon Composite Welderâ„¢ Methacrylate Adhesive FS, Blue Green, Black Information provided by ITW Devcon |
|||
| Cure Time | 4.00 - 5.00 min | 0.0667 - 0.0833 hour | Working time |
| ITW Devcon Metal Welderâ„¢ Methacrylate Adhesive, Grey / Beads Information provided by ITW Devcon |
|||
| Cure Time | 4.00 - 6.00 min | 0.0667 - 0.100 hour | Working time |
| ITW Devcon Plastic Welderâ„¢ Methacrylate Adhesive SD, Off-White Information provided by ITW Devcon |
|||
| Cure Time | 4.00 - 6.00 min | 0.0667 - 0.100 hour | Working time |
| ITW Devcon Plastic Welderâ„¢ Methacrylate Adhesive, Straw, White, Black Information provided by ITW Devcon |
|||
| Cure Time | 4.00 min | 0.0667 hour | Tack Free Time |
| Shin-Etsu Silicones KE-347T Silicone, RTV Coating Information Provided by Shin-Etsu Silicones of America, Inc. |
|||
| Cure Time | 4.00 min @Temperature 177 °C |
0.0667 hour @Temperature 350 °F |
|
| TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 84A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
| Cure Time | 4.00 min @Temperature 177 °C |
0.0667 hour @Temperature 350 °F |
|
| TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 350ºF Cure Temperature Millathane® 76 is a very suitable choice for use in products such as bushings, small copier rolls; automotive applications — bumpers, o-rings, hydraulic seals, belts, gaskets, solid tires — and m.. |
|||
| Cure Time | 4.00 min | 0.0667 hour | ts2, Target; ASTM D2084 |
| ExxonMobil Exxon™ 2211 Fast Cure Rate Grade Exxon Bromobutyl is a brominated copolymer of isobutylene and isoprene. The product form is offwhite to amber balesInformation provided by ExxonMobil Chemical |
|||
| Cure Time | 4.00 - 10.0 min | 0.0667 - 0.167 hour | t`50; ASTM D2084 |
| ExxonMobil Exxon™ 2211 Fast Cure Rate Grade Exxon Bromobutyl is a brominated copolymer of isobutylene and isoprene. The product form is offwhite to amber balesInformation provided by ExxonMobil Chemical |
|||
| Cure Time | 4.00 min | 0.0667 hour | ts2, Target; ASTM D2084 |
| ExxonMobil Exxon™ 2222 Regular Cure Rate Grade Exxon Bromobutyl is a brominated copolymer of isobutylene and isoprene. The product for is white to light amber bales.Information provided by ExxonMobil Chemical |
|||
| Cure Time | 4.00 min | 0.0667 hour | ts2, Target; ASTM D2084 |
| ExxonMobil Exxon™ 2235 Regular Cure Rate Grade Exxon Bromobutyl is a brominated copolymer of isobutylene and isoprene. The product form is white to light amber bales.Information provided by ExxonMobil Chemical |
|||
| Cure Time | 4.00 min | 0.0667 hour | ts2, Target; ASTM D2084 |
| ExxonMobil Exxon™ 2255 Regular Cure Rate Grade Exxon Bromobutyl is a brominated copolymer of isobutylene and isoprene.The product form is white to light amber bales.Information provided by ExxonMobil Chemical |
|||
| Cure Time | 4.00 min | 0.0667 hour | Curelastmeter |
| Daikin DAI-EL G-702 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content Offers minimal compression set and excellent sealing. The copolymer type offers good compression set characteristics.Features: General purpose with excellent elongation and tear strength.Informatio.. |
|||
| Cure Time | 4.00 min | 0.0667 hour | Tack-Free, 10 g, 1/4" thick @ RT |
| 3M Scotch-Weld™ DP600 Concrete Repair and Self-Leveling 3M™ Scotch-Weld™ Concrete Repair Self-Leveling DP600 is a gray, rapid setting, two component polyurethane. It is packaged as a 1:1 ratio liquid in a duo-pack cartridge. With the squeeze of a trigg.. |
|||
| Cure Time | 4.00 min | 0.0667 hour | Time to Handling Strength |
| 3M Scotch-Weld™ DP601 Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are gray, rapid, setting, two component polyurethanes. They are packaged as 1:1 ratio liquids in a duo-pack cartridge. With the squeeze of a trigger, the compon.. |
|||
| Cure Time | 4.00 min @Temperature 177 °C |
0.0667 hour @Temperature 350 °F |
|
| TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 84A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||