Polymer Property : Electrical Resistivity = 0.0001278 ohm-cm Product List

Electrical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Electrical Properties	Metric	English
Electrical Resistivity	0.0001278 ohm-cm @Temperature 1100 Â°C	0.0001278 ohm-cm @Temperature 2010 Â°F
Haynes HR-120Â® alloy, solution heat-treated Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Electrical Resistivity	0.0001278 ohm-cm @Temperature 1100 Â°C	0.0001278 ohm-cm @Temperature 2010 Â°F
Haynes HR-120Â® alloy, solution heat-treated aged at 1200Â°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Electrical Resistivity	0.0001278 ohm-cm @Temperature 1100 Â°C	0.0001278 ohm-cm @Temperature 2010 Â°F
Haynes HR-120Â® alloy, solution heat-treated aged at 1400Â°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Electrical Resistivity	0.0001278 ohm-cm @Temperature 1100 Â°C	0.0001278 ohm-cm @Temperature 2010 Â°F
Haynes HR-120Â® alloy, solution heat-treated aged at 1600Â°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Electrical Resistivity	0.0001278 ohm-cm @Temperature 1100 Â°C	0.0001278 ohm-cm @Temperature 2010 Â°F
Haynes HR-120Â® alloy, solution heat-treated aged at 1800Â°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Electrical Resistivity	0.0001278 ohm-cm @Temperature 1100 Â°C	0.0001278 ohm-cm @Temperature 2010 Â°F
Haynes HR-120Â® alloy, solution heat-treated plate Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Electrical Resistivity	0.0001278 ohm-cm	0.0001278 ohm-cm
Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened, after long term high temperature exposure Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b..