Haynes HR-120® alloy, solution heat-treated plate

Category Metal , Superalloy , Iron Base
Manufacturer Haynes International, Inc.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes HR-120® alloy, solution heat-treated plate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts and basket liners, muffles and retorts, heat treating fixtures, waste incinerators, radiant tubes, cast link belt pins, recuperators, and fluidized bed components.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.07 g/cc
0.292 lb/in³
at RT.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 735 MPa
107000 psi
34.0 MPa

@Temperature 1205 °C
 4930 psi

@Temperature 2201 °F
105 MPa

@Temperature 1095 °C
 15200 psi

@Temperature 2003 °F
190 MPa

@Temperature 980 °C
 27600 psi

@Temperature 1800 °F
325 MPa

@Temperature 870 °C
 47100 psi

@Temperature 1600 °F
440 MPa

@Temperature 760 °C
 63800 psi

@Temperature 1400 °F
505 MPa

@Temperature 650 °C
 73200 psi

@Temperature 1200 °F
555 MPa

@Temperature 540 °C
 80500 psi

@Temperature 1000 °F
Tensile Strength, Yield 375 MPa

@Strain 0.200 %
 54400 psi

@Strain 0.200 %
27.0 MPa

@Strain 0.200 %,
Temperature 1205 °C
 3920 psi

@Strain 0.200 %,
Temperature 2201 °F
63.0 MPa

@Strain 0.200 %,
Temperature 1095 °C
 9140 psi

@Strain 0.200 %,
Temperature 2003 °F
135 MPa

@Strain 0.200 %,
Temperature 980 °C
 19600 psi

@Strain 0.200 %,
Temperature 1800 °F
170 MPa

@Strain 0.200 %,
Temperature 650 °C
 24700 psi

@Strain 0.200 %,
Temperature 1200 °F
175 MPa

@Strain 0.200 %,
Temperature 760 °C
 25400 psi

@Strain 0.200 %,
Temperature 1400 °F
175 MPa

@Strain 0.200 %,
Temperature 540 °C
 25400 psi

@Strain 0.200 %,
Temperature 1000 °F
185 MPa

@Strain 0.200 %,
Temperature 870 °C
 26800 psi

@Strain 0.200 %,
Temperature 1600 °F
Elongation at Break 50 %
50 %
in 50.8 mm
50 %

@Temperature 760 °C
 50 %

@Temperature 1400 °F
 in 50.8 mm
51 %

@Temperature 870 °C
 51 %

@Temperature 1600 °F
 in 50.8 mm
60 %

@Temperature 650 °C
 60 %

@Temperature 1200 °F
 in 50.8 mm
61 %

@Temperature 540 °C
 61 %

@Temperature 1000 °F
 in 50.8 mm
81 %

@Temperature 980 °C
 81 %

@Temperature 1800 °F
 in 50.8 mm
89 %

@Temperature 1095 °C
 89 %

@Temperature 2003 °F
 in 50.8 mm
89 %

@Temperature 1205 °C
 89 %

@Temperature 2201 °F
 in 50.8 mm
Modulus of Elasticity 197 GPa
28600 ksi
RT
128 GPa

@Temperature 1000 °C
 18600 ksi

@Temperature 1830 °F
136 GPa

@Temperature 900 °C
 19700 ksi

@Temperature 1650 °F
143 GPa

@Temperature 800 °C
 20700 ksi

@Temperature 1470 °F
152 GPa

@Temperature 700 °C
 22000 ksi

@Temperature 1290 °F
159 GPa

@Temperature 600 °C
 23100 ksi

@Temperature 1110 °F
165 GPa

@Temperature 500 °C
 23900 ksi

@Temperature 932 °F
174 GPa

@Temperature 400 °C
 25200 ksi

@Temperature 752 °F
182 GPa

@Temperature 300 °C
 26400 ksi

@Temperature 572 °F
188 GPa

@Temperature 200 °C
 27300 ksi

@Temperature 392 °F
194 GPa

@Temperature 100 °C
 28100 ksi

@Temperature 212 °F
Thermal Properties Metric English Comments
CTE, linear 14.3 µm/m-°C

@Temperature 25.0 - 100 °C
 7.94 µin/in-°F

@Temperature 77.0 - 212 °F
14.9 µm/m-°C

@Temperature 25.0 - 200 °C
 8.28 µin/in-°F

@Temperature 77.0 - 392 °F
15.3 µm/m-°C

@Temperature 25.0 - 300 °C
 8.50 µin/in-°F

@Temperature 77.0 - 572 °F
15.8 µm/m-°C

@Temperature 25.0 - 400 °C
 8.78 µin/in-°F

@Temperature 77.0 - 752 °F
16.1 µm/m-°C

@Temperature 25.0 - 500 °C
 8.94 µin/in-°F

@Temperature 77.0 - 932 °F
16.4 µm/m-°C

@Temperature 25.0 - 600 °C
 9.11 µin/in-°F

@Temperature 77.0 - 1110 °F
16.9 µm/m-°C

@Temperature 25.0 - 700 °C
 9.39 µin/in-°F

@Temperature 77.0 - 1290 °F
17.3 µm/m-°C

@Temperature 25.0 - 800 °C
 9.61 µin/in-°F

@Temperature 77.0 - 1470 °F
17.6 µm/m-°C

@Temperature 25.0 - 900 °C
 9.78 µin/in-°F

@Temperature 77.0 - 1650 °F
17.8 µm/m-°C

@Temperature 25.0 - 1000 °C
 9.89 µin/in-°F

@Temperature 77.0 - 1830 °F
Specific Heat Capacity 0.467 J/g-°C
0.112 BTU/lb-°F
RT
0.483 J/g-°C

@Temperature 100 °C
 0.115 BTU/lb-°F

@Temperature 212 °F
0.500 J/g-°C

@Temperature 200 °C
 0.120 BTU/lb-°F

@Temperature 392 °F
0.522 J/g-°C

@Temperature 300 °C
 0.125 BTU/lb-°F

@Temperature 572 °F
0.531 J/g-°C

@Temperature 400 °C
 0.127 BTU/lb-°F

@Temperature 752 °F
0.558 J/g-°C

@Temperature 500 °C
 0.133 BTU/lb-°F

@Temperature 932 °F
0.607 J/g-°C

@Temperature 600 °C
 0.145 BTU/lb-°F

@Temperature 1110 °F
0.647 J/g-°C

@Temperature 700 °C
 0.155 BTU/lb-°F

@Temperature 1290 °F
0.655 J/g-°C

@Temperature 800 °C
 0.157 BTU/lb-°F

@Temperature 1470 °F
0.660 J/g-°C

@Temperature 900 °C
 0.158 BTU/lb-°F

@Temperature 1650 °F
0.663 J/g-°C

@Temperature 1000 °C
 0.158 BTU/lb-°F

@Temperature 1830 °F
0.667 J/g-°C

@Temperature 1100 °C
 0.159 BTU/lb-°F

@Temperature 2010 °F
0.671 J/g-°C

@Temperature 1200 °C
 0.160 BTU/lb-°F

@Temperature 2190 °F
Thermal Conductivity 11.4 W/m-K
79.1 BTU-in/hr-ft²-°F
RT
12.6 W/m-K

@Temperature 100 °C
 87.4 BTU-in/hr-ft²-°F

@Temperature 212 °F
Electrical Properties Metric English Comments
Electrical Resistivity 0.0001052 ohm-cm
0.0001052 ohm-cm
RT
0.0001231 ohm-cm

@Temperature 700 °C
 0.0001231 ohm-cm

@Temperature 1290 °F
0.0001245 ohm-cm

@Temperature 800 °C
 0.0001245 ohm-cm

@Temperature 1470 °F
0.0001257 ohm-cm

@Temperature 900 °C
 0.0001257 ohm-cm

@Temperature 1650 °F
0.0001266 ohm-cm

@Temperature 1000 °C
 0.0001266 ohm-cm

@Temperature 1830 °F
0.0001278 ohm-cm

@Temperature 1100 °C
 0.0001278 ohm-cm

@Temperature 2010 °F
0.0001287 ohm-cm

@Temperature 1200 °C
 0.0001287 ohm-cm

@Temperature 2190 °F