- Polymer Property : Electrical Resistivity = 0.000135 ohm-cm
Polymer Property : Electrical Resistivity = 0.000135 ohm-cm Product List
Electrical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 300 °C |
0.000135 ohm-cm @Temperature 572 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 1000 °C |
0.000135 ohm-cm @Temperature 1830 °F |
|
| Haynes 625 alloy, 20% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 300 °C |
0.000135 ohm-cm @Temperature 572 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 300 °C |
0.000135 ohm-cm @Temperature 572 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 1000 °C |
0.000135 ohm-cm @Temperature 1830 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 1000 °C |
0.000135 ohm-cm @Temperature 1830 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 300 °C |
0.000135 ohm-cm @Temperature 572 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 1000 °C |
0.000135 ohm-cm @Temperature 1830 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 300 °C |
0.000135 ohm-cm @Temperature 572 °F |
|
| Haynes 625 alloy, cold rolled and 1050°C mill-annealed sheet Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 300 °C |
0.000135 ohm-cm @Temperature 572 °F |
|
| Haynes 625 alloy, hot rolled and 1050°C mill-annealed plate Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 1000 °C |
0.000135 ohm-cm @Temperature 1830 °F |
|
| Haynes 625 alloy, hot rolled and 1050°C mill-annealed plate Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 1000 °C |
0.000135 ohm-cm @Temperature 1830 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 300 °C |
0.000135 ohm-cm @Temperature 572 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 1000 °C |
0.000135 ohm-cm @Temperature 1830 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 300 °C |
0.000135 ohm-cm @Temperature 572 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 1000 °C |
0.000135 ohm-cm @Temperature 1830 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 1000 °C |
0.000135 ohm-cm @Temperature 1830 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 1000 °C |
0.000135 ohm-cm @Temperature 1830 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 1000 °C |
0.000135 ohm-cm @Temperature 1830 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000135 ohm-cm | 0.000135 ohm-cm | |
| TIMET TIMETAL® 21S Titanium Alloy (Ti-15Mo-3Nb-3Al-0.2Si, ASTM Grade 21); Annealed Strip/Sheet High-Strength, Oxidation Resistant Strip AlloyFeatures: Offers the good cold formability and weldability of a beta strip alloy, but with greatly improved oxidation resistance and creep strength. Aer.. |
|||
| Electrical Resistivity | 0.000135 ohm-cm | 0.000135 ohm-cm | |
| Goodfellow Iron 81/Boron 13.5/Silicon 3.5 Alloy Information provided by Goodfellow. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 300 °C |
0.000135 ohm-cm @Temperature 572 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 300 °C |
0.000135 ohm-cm @Temperature 572 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 300 °C |
0.000135 ohm-cm @Temperature 572 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var.. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 1000 °C |
0.000135 ohm-cm @Temperature 1830 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var.. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 1000 °C |
0.000135 ohm-cm @Temperature 1830 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Electrical Resistivity | 0.000135 ohm-cm @Temperature 1000 °C |
0.000135 ohm-cm @Temperature 1830 °F |
|
| Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||