Haynes 625 alloy, cold rolled and 1050°C mill-annealed sheet

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer Haynes International, Inc.
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes 625 alloy, cold rolled and 1050°C mill-annealed sheet.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of high-temperature aerospace, chemical process industry and power industry uses. Widely used in sea water and power plant scrubber applications.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.44 g/cc
0.305 lb/in³
at RT
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 905 MPa
131000 psi
95.0 MPa

@Temperature 1095 °C
 13800 psi

@Temperature 2003 °F
165 MPa

@Temperature 980 °C
 23900 psi

@Temperature 1800 °F
345 MPa

@Temperature 870 °C
 50000 psi

@Temperature 1600 °F
600 MPa

@Temperature 760 °C
 87000 psi

@Temperature 1400 °F
760 MPa

@Temperature 650 °C
 110000 psi

@Temperature 1200 °F
770 MPa

@Temperature 540 °C
 112000 psi

@Temperature 1000 °F
Tensile Strength, Yield 490 MPa

@Strain 0.200 %
 71100 psi

@Strain 0.200 %
39.0 MPa

@Strain 0.200 %,
Temperature 1095 °C
 5660 psi

@Strain 0.200 %,
Temperature 2003 °F
83.0 MPa

@Strain 0.200 %,
Temperature 980 °C
 12000 psi

@Strain 0.200 %,
Temperature 1800 °F
205 MPa

@Strain 0.200 %,
Temperature 870 °C
 29700 psi

@Strain 0.200 %,
Temperature 1600 °F
345 MPa

@Strain 0.200 %,
Temperature 760 °C
 50000 psi

@Strain 0.200 %,
Temperature 1400 °F
370 MPa

@Strain 0.200 %,
Temperature 540 °C
 53700 psi

@Strain 0.200 %,
Temperature 1000 °F
370 MPa

@Strain 0.200 %,
Temperature 650 °C
 53700 psi

@Strain 0.200 %,
Temperature 1200 °F
Elongation at Break 48.5 %
48.5 %
in 50.8 mm
43.8 %

@Temperature 980 °C
 43.8 %

@Temperature 1800 °F
 in 50.8 mm
44.7 %

@Temperature 1095 °C
 44.7 %

@Temperature 2003 °F
 in 50.8 mm
45.9 %

@Temperature 870 °C
 45.9 %

@Temperature 1600 °F
 in 50.8 mm
53.1 %

@Temperature 760 °C
 53.1 %

@Temperature 1400 °F
 in 50.8 mm
54 %

@Temperature 540 °C
 54 %

@Temperature 1000 °F
 in 50.8 mm
55.6 %

@Temperature 650 °C
 55.6 %

@Temperature 1200 °F
 in 50.8 mm
Modulus of Elasticity 208 GPa
30200 ksi
RT
126 GPa

@Temperature 1000 °C
 18300 ksi

@Temperature 1830 °F
142 GPa

@Temperature 900 °C
 20600 ksi

@Temperature 1650 °F
153 GPa

@Temperature 800 °C
 22200 ksi

@Temperature 1470 °F
163 GPa

@Temperature 700 °C
 23600 ksi

@Temperature 1290 °F
171 GPa

@Temperature 600 °C
 24800 ksi

@Temperature 1110 °F
179 GPa

@Temperature 500 °C
 26000 ksi

@Temperature 932 °F
186 GPa

@Temperature 400 °C
 27000 ksi

@Temperature 752 °F
192 GPa

@Temperature 300 °C
 27800 ksi

@Temperature 572 °F
199 GPa

@Temperature 200 °C
 28900 ksi

@Temperature 392 °F
201 GPa

@Temperature 100 °C
 29200 ksi

@Temperature 212 °F
Thermal Properties Metric English Comments
CTE, linear 12.8 µm/m-°C

@Temperature 25.0 - 100 °C
 7.11 µin/in-°F

@Temperature 77.0 - 212 °F
13.1 µm/m-°C

@Temperature 25.0 - 200 °C
 7.28 µin/in-°F

@Temperature 77.0 - 392 °F
13.4 µm/m-°C

@Temperature 25.0 - 300 °C
 7.44 µin/in-°F

@Temperature 77.0 - 572 °F
13.8 µm/m-°C

@Temperature 25.0 - 400 °C
 7.67 µin/in-°F

@Temperature 77.0 - 752 °F
14.2 µm/m-°C

@Temperature 25.0 - 500 °C
 7.89 µin/in-°F

@Temperature 77.0 - 932 °F
14.8 µm/m-°C

@Temperature 25.0 - 600 °C
 8.22 µin/in-°F

@Temperature 77.0 - 1110 °F
15.4 µm/m-°C

@Temperature 25.0 - 700 °C
 8.56 µin/in-°F

@Temperature 77.0 - 1290 °F
16.0 µm/m-°C

@Temperature 25.0 - 800 °C
 8.89 µin/in-°F

@Temperature 77.0 - 1470 °F
16.7 µm/m-°C

@Temperature 25.0 - 900 °C
 9.28 µin/in-°F

@Temperature 77.0 - 1650 °F
17.4 µm/m-°C

@Temperature 25.0 - 1000 °C
 9.67 µin/in-°F

@Temperature 77.0 - 1830 °F
Specific Heat Capacity 0.410 J/g-°C
0.0980 BTU/lb-°F
RT
0.428 J/g-°C

@Temperature 100 °C
 0.102 BTU/lb-°F

@Temperature 212 °F
0.455 J/g-°C

@Temperature 200 °C
 0.109 BTU/lb-°F

@Temperature 392 °F
0.477 J/g-°C

@Temperature 300 °C
 0.114 BTU/lb-°F

@Temperature 572 °F
0.503 J/g-°C

@Temperature 400 °C
 0.120 BTU/lb-°F

@Temperature 752 °F
0.527 J/g-°C

@Temperature 500 °C
 0.126 BTU/lb-°F

@Temperature 932 °F
0.552 J/g-°C

@Temperature 600 °C
 0.132 BTU/lb-°F

@Temperature 1110 °F
0.576 J/g-°C

@Temperature 700 °C
 0.138 BTU/lb-°F

@Temperature 1290 °F
0.600 J/g-°C

@Temperature 800 °C
 0.143 BTU/lb-°F

@Temperature 1470 °F
0.625 J/g-°C

@Temperature 900 °C
 0.149 BTU/lb-°F

@Temperature 1650 °F
0.648 J/g-°C

@Temperature 1000 °C
 0.155 BTU/lb-°F

@Temperature 1830 °F
Thermal Conductivity 9.80 W/m-K
68.0 BTU-in/hr-ft²-°F
RT
10.9 W/m-K

@Temperature 100 °C
 75.6 BTU-in/hr-ft²-°F

@Temperature 212 °F
Electrical Properties Metric English Comments
Electrical Resistivity 0.000129 ohm-cm
0.000129 ohm-cm
RT
0.000132 ohm-cm

@Temperature 100 °C
 0.000132 ohm-cm

@Temperature 212 °F
0.000134 ohm-cm

@Temperature 200 °C
 0.000134 ohm-cm

@Temperature 392 °F
0.000135 ohm-cm

@Temperature 300 °C
 0.000135 ohm-cm

@Temperature 572 °F
0.000135 ohm-cm

@Temperature 1000 °C
 0.000135 ohm-cm

@Temperature 1830 °F
0.000136 ohm-cm

@Temperature 900 °C
 0.000136 ohm-cm

@Temperature 1650 °F
0.000136 ohm-cm

@Temperature 400 °C
 0.000136 ohm-cm

@Temperature 752 °F
0.000137 ohm-cm

@Temperature 500 °C
 0.000137 ohm-cm

@Temperature 932 °F
0.000137 ohm-cm

@Temperature 800 °C
 0.000137 ohm-cm

@Temperature 1470 °F
0.000138 ohm-cm

@Temperature 600 °C
 0.000138 ohm-cm

@Temperature 1110 °F
0.000138 ohm-cm

@Temperature 700 °C
 0.000138 ohm-cm

@Temperature 1290 °F