- HOME
- POLYMER SEARCH
- Polymer Property : Electrical Resistivity = 0.000138 ohm-cm
Polymer Property : Electrical Resistivity = 0.000138 ohm-cm Product List
Electrical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 700 °C |
0.000138 ohm-cm @Temperature 1290 °F |
|
| Haynes 625 alloy, 0% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 700 °C |
0.000138 ohm-cm @Temperature 1290 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 700 °C |
0.000138 ohm-cm @Temperature 1290 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 600 °C |
0.000138 ohm-cm @Temperature 1110 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 600 °C |
0.000138 ohm-cm @Temperature 1110 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 700 °C |
0.000138 ohm-cm @Temperature 1290 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 600 °C |
0.000138 ohm-cm @Temperature 1110 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 700 °C |
0.000138 ohm-cm @Temperature 1290 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 600 °C |
0.000138 ohm-cm @Temperature 1110 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 700 °C |
0.000138 ohm-cm @Temperature 1290 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 700 °C |
0.000138 ohm-cm @Temperature 1290 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 700 °C |
0.000138 ohm-cm @Temperature 1290 °F |
|
| Haynes 625 alloy, cold rolled and 1050°C mill-annealed sheet Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 600 °C |
0.000138 ohm-cm @Temperature 1110 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 700 °C |
0.000138 ohm-cm @Temperature 1290 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 700 °C |
0.000138 ohm-cm @Temperature 1290 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 600 °C |
0.000138 ohm-cm @Temperature 1110 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 700 °C |
0.000138 ohm-cm @Temperature 1290 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 700 °C |
0.000138 ohm-cm @Temperature 1290 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 600 °C |
0.000138 ohm-cm @Temperature 1110 °F |
|
| Haynes 625 alloy, plate, as annealed at 1025°C, rapid cooled Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 300 °C |
0.000138 ohm-cm @Temperature 572 °F |
|
| Haynes Hastelloy® B-3® alloy, 0% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 400 °C |
0.000138 ohm-cm @Temperature 752 °F |
|
| Haynes Hastelloy® B-3® alloy, 10% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 300 °C |
0.000138 ohm-cm @Temperature 572 °F |
|
| Haynes Hastelloy® B-3® alloy, 3.2 mm bright annealed sheet The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 300 °C |
0.000138 ohm-cm @Temperature 572 °F |
|
| Haynes Hastelloy® B-3® alloy, 40% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 600 °C |
0.000138 ohm-cm @Temperature 1110 °F |
|
| Haynes 625 alloy, 30% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 700 °C |
0.000138 ohm-cm @Temperature 1290 °F |
|
| Haynes 625 alloy, 30% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 700 °C |
0.000138 ohm-cm @Temperature 1290 °F |
|
| Haynes 625 alloy, 50% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 700 °C |
0.000138 ohm-cm @Temperature 1290 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 600 °C |
0.000138 ohm-cm @Temperature 1110 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Electrical Resistivity | 0.000138 ohm-cm @Temperature 600 °C |
0.000138 ohm-cm @Temperature 1110 °F |
|
| Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||