Polymer Property : Hot Wire Ignition, HWI = 0.00 sec Product List

Electrical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Electrical Properties	Metric	English	Comments
Hot Wire Ignition, HWI	>= 0.00 sec @Thickness 3.05 mm	>= 0.00 sec @Thickness 0.120 in	UL PLC 0
Resinoid 7051 Phenolic Molding, Glass Reinforced Data provided by the manufacturer.The Resinoid 1300 and 7000 glass fiber reinforced series compounds feature mechanical strength, dimensional stability, electrical insulation, and heat resistance
Hot Wire Ignition, HWI	0.00 - 7.0 sec @Thickness 1.50 mm	0.00 - 7.0 sec @Thickness 0.0591 in	UL 746A
Idemitsu Kosan XarecÂ® N WA 7020 SPS, 20% Glass Filled Crystalline Polymer Blend, Glass Filled, Impact Modified. Used in Automotive Electronics applications.
Hot Wire Ignition, HWI	0.00 - 2.0 sec	0.00 - 2.0 sec	UL 746A
SABIC Innovative Plastics LNP VERTON RV00AES PA 66 (Europe-Africa-Middle East) LNP VERTON* RV00AES is a compound based on PA 66 resin containing Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized.
Hot Wire Ignition, HWI	0.00 - 2.0 sec	0.00 - 2.0 sec	UL 746A
SABIC Innovative Plastics LNP VERTON RV00AESS PA 66 (Europe-Africa-Middle East) LNP* VERTON* RV00AESS is a compound based on PA 66 resin containing Long Glass Fiber. Added features include; Easy Molding, Heat Stabilized.
Hot Wire Ignition, HWI	0.00 - 7.0 sec	0.00 - 7.0 sec	UL 746A
SABIC Innovative Plastics NORYL GFN1 PPE+PS PPE+PS blend. 10% Glass reinforced. NSF 61 listing in several colors (restrictions apply). FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Sui..
Hot Wire Ignition, HWI	0.00 sec @Thickness >=0.750 mm	0.00 sec @Thickness >=0.0295 in	ASTM D3874-88
BASF Ultramid® A3XZG5 BK 23187 25% Glass Filled PA66 FR (Conditioned) Description: Impact-modified, 25% glass-fiber reinforced injection-molding grade with improved flame retardance and enhanced long-term stability. Flame retardant based on red phosphorus; for compone..
Hot Wire Ignition, HWI	>= 0.00 sec @Thickness 3.05 mm	>= 0.00 sec @Thickness 0.120 in	UL PLC 0
Resinoid 2016 Phenolic Molding, Fabric Reinforced Data provided by the manufacturer.The Resinoid 2000 organic fiber reinforced series compounds feature mechanical strength, dimensional stability, and shock resistance
Hot Wire Ignition, HWI	>= 0.00 sec @Thickness 3.05 mm	>= 0.00 sec @Thickness 0.120 in	UL PLC 0
Resinoid 7201 Phenolic Molding, Glass Reinforced Data provided by the manufacturer.The Resinoid 1300 and 7000 glass fiber reinforced series compounds feature mechanical strength, dimensional stability, electrical insulation, and heat resistance