3M Fastbond™ 49 Insulation Adhesive

Category Polymer , Adhesive
Manufacturer 3M
Trade Name Fastbond™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Fastbond™ 49 Insulation Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Fastbond™ Insulation Adhesive 49 is a water-based, high solids, fast tacking, pressure sensitive adhesive for bonding lightweight materials like fiberglass insulation, felt, shoddy, paper and other materials to metal and many other surfaces.Information provided by 3M
Physical Properties Metric English Comments
Solids Content 53 - 57 %
53 - 57 %
Brookfield Viscosity 450 - 650 cP
450 - 650 cP
RVF #3 sp @ 20 rpm @ 25°C
Mechanical Properties Metric English Comments
Shear Strength 0.0827 MPa
12.0 psi
Neoprene Rubber, after 48 hrs at 23°C
0.0965 MPa
14.0 psi
EPDM, after 48 hrs at 23°C
0.234 MPa
34.0 psi
HDPE, after 48 hrs at 23°C
0.269 MPa
39.0 psi
Polypropylene, after 48 hrs at 23°C
0.345 MPa
50.0 psi
ABS Plastic, after 48 hrs at 23°C
0.352 MPa
51.0 psi
2024 T3 Aluminum, after 48 hrs at 23°C
0.359 MPa
52.0 psi
Clad Aluminum, after 48 hrs at 23°C
0.359 MPa
52.0 psi
Stainless Steel, after 48 hrs at 23°C
0.359 MPa
52.0 psi
Acrylic, after 48 hrs at 23°C
0.365 MPa
53.0 psi
Glass, after 48 hrs at 23°C
0.365 MPa
53.0 psi
High Impact Polystyrene, after 48 hrs at 23°C
0.386 MPa
56.0 psi
PVC, after 48 hrs at 23°C
0.393 MPa
57.0 psi
Cold Rolled Steel, after 48 hrs at 23°C
0.393 MPa
57.0 psi
Polycarbonate, after 48 hrs at 23°C
Peel Strength 0.0877 kN/m
0.500 pli
HDPE, 180°, after 48 hrs at 23°C
0.175 kN/m
1.00 pli
EPDM, 180°, after 48 hrs at 23°C
0.228 kN/m
1.30 pli
Neoprene Rubber, 180°, after 48 hrs at 23°C
0.280 kN/m
1.60 pli
Glass, 180°, after 48 hrs at 23°C
0.386 kN/m
2.20 pli
Polypropylene, 180°, after 48 hrs at 23°C
0.403 kN/m
2.30 pli
2024 T3 Aluminum, 180°, after 48 hrs at 23°C
0.491 kN/m
2.80 pli
Clad Aluminum, 180°, after 48 hrs at 23°C
0.526 kN/m
3.00 pli
Cold Rolled Steel, 180°, after 48 hrs at 23°C
0.561 kN/m
3.20 pli
Stainless Steel, 180°, after 48 hrs at 23°C
0.684 kN/m
3.90 pli
Acrylic, 180°, after 48 hrs at 23°C
0.789 kN/m
4.50 pli
PVC, 180°, after 48 hrs at 23°C
0.824 kN/m
4.70 pli
ABS Plastic, 180°, after 48 hrs at 23°C
0.912 kN/m
5.20 pli
Polycarbonate, 180°, after 48 hrs at 23°C
0.982 kN/m
5.60 pli
High Impact Polystyrene, 180°, after 48 hrs at 23°C
Descriptive Properties Value Comments
Appearance Milky White (wet), Clear (dry)
Base Acrylate