Arkema Group Rilsan® ASR 30 Nylon 12, 30% Carbon Fiber Filled (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, Carbon Fiber Filled
Manufacturer Arkema
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Rilsan® ASR 30 Nylon 12, 30% Carbon Fiber Filled (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation ISO 1874-PA12,M,16-120,CF30Rigid grade with carbon fiber filler (30%) for injection molding. Available color: black.Very high rigidity. High strength-to-weight ratio. Very low shrinkage: include 0,5% on average for the design of the mold. High dimensional stability (low moisture absorption). Antistatic properties.Example applications: Parts with high mechanical properties and dimensional precision.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.15 g/cc
0.0415 lb/in³
Melt Flow 3.0 g/10 min

@Load 2.16 kg,
Temperature 235 °C
3.0 g/10 min

@Load 4.76 lb,
Temperature 455 °F
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 161 MPa
23400 psi
5 mm/min
Elongation at Break 3.0 %
3.0 %
5 mm/min
Tensile Modulus 15.0 GPa
2180 ksi
1 mm/min
Charpy Impact Unnotched 6.12 J/cm²
29.1 ft-lb/in²
5.91 J/cm²

@Temperature -30.0 °C
28.1 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 1.45 J/cm²
6.90 ft-lb/in²
0.940 J/cm²

@Temperature -30.0 °C
4.47 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
Melting Point 174 °C
345 °F
10°C/min
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.10 mm
HB

@Thickness 0.122 in