BASF Capron® 5202CQ Blend HS Blend Nylon 66 (Conditioned)  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Capron® 5202CQ Blend HS Blend Nylon 66 (Conditioned)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Capron 5202CQ HS Blend is a heat stabilized, blended polyamide 6,6 injection molding homopolymer developed for fast molding cycles. It is also available in pigmented versions.Capron 5202CQ HS Blend is generally recommended for applications such as aerosol valve bodies, stems, and actuators.Data provided by Allied Signal.Processing: Max. water content 0.25%. Product is supplied in sealed containers and drying is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 85°C (185 °F). Is recommended. Drying time is dependent on moisture level.Melt Temperature: 280-305 degC (536-581 degF). Mold Temperature: 80-95 degC (176-203 degF). Injection and Packing Pressure: 35-125 bar (500-1500psi) A mold temperature of 80-95 degC (176-203 degF) is recommended, but temperatures of as low as 45 degC (113 degF) and as high as 105 degC (221 degF) can be used where applicable. Injection pressure controls the filling of the part and should be applied for 90% of ram travel. Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off. Fast fill rates are recommended to insure uniform melt delivery to the cavity and prevent premature freezing.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
(Dry)
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 45.0 MPa
6530 psi
ASTM data at 5 mm/min.
Tensile Strength, Yield 59.0 MPa
8560 psi
ISO value at 50 mm/min.
60.0 MPa
8700 psi
ASTM value at 50 mm/min.
Elongation at Break >= 50 %
>= 50 %
Nominal
70 %
70 %
ASTM, 5 mm/minl
Elongation at Yield 18 %
18 %
ISO Value at 50 mm/min.
20 %
20 %
ASTM Value at 50 mm/min.
Tensile Modulus 1.70 GPa
247 ksi
same value from ASTM and ISO test.
Thermal Properties Metric English Comments
Melting Point 260 °C
500 °F
(Dry)
Processing Properties Metric English Comments
Processing Temperature 290 °C
554 °F
See Materials Notes
Mold Temperature 80.0 °C
176 °F
See Materials Notes
Drying Temperature 85.0 °C
185 °F
See Materials Notes