Carpenter Pyromet® CTX-3 Superalloy, Heat Treatment for Brazing Cycles over 982°C

Category Metal , Superalloy , Iron Base
Manufacturer Carpenter Technology Corporation (Cartech)
Trade Name Pyromet®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Carpenter Pyromet® CTX-3 Superalloy, Heat Treatment for Brazing Cycles over 982°C.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by Carpenter Technology Corporation.Pyromet® alloy CTX-3 is a high strength, precipitation hardenable superalloy which exhibits a low CTE over a broad temperature range. This alloy also possess high hot hardness and good thermal fatigue resistance. It is weldable, brazable, and can be chromium plated. This material offers significant improvement in notched stress-rupture strength over Pyromet alloy CTX-1. Retained hot-cold work is not required for good stress rupture properties and is not affected by stress orientation.Pyromet® is a registered trademark of Carpenter Technology Corporation.
Physical Properties Metric English Comments
Density 8.28 g/cc
0.299 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1160 MPa
168000 psi
Tensile Strength, Yield 760 MPa

@Strain 0.200 %
110000 psi

@Strain 0.200 %
Elongation at Break 9.0 %
9.0 %
In 50 mm
Reduction of Area 14 %
14 %
Modulus of Elasticity 159.9 GPa
23190 ksi
Thermal Properties Metric English Comments
CTE, linear 7.50 µm/m-°C

@Temperature 25.0 - 416 °C
4.17 µin/in-°F

@Temperature 77.0 - 781 °F
7.70 µm/m-°C

@Temperature 25.0 - 260 °C
4.28 µin/in-°F

@Temperature 77.0 - 500 °F
Component Elements Properties Metric English Comments
Aluminum, Al <= 0.25 %
<= 0.25 %
Boron, B <= 0.012 %
<= 0.012 %
Carbon, C <= 0.050 %
<= 0.050 %
Chromium, Cr <= 0.50 %
<= 0.50 %
Cobalt, Co 13 - 15 %
13 - 15 %
Copper, Cu <= 0.50 %
<= 0.50 %
Iron, Fe 39 %
39 %
as remainder
Manganese, Mn <= 0.50 %
<= 0.50 %
Nb + Ta 4.5 - 5.5 %
4.5 - 5.5 %
Nickel, Ni 37 - 39 %
37 - 39 %
Niobium, Nb (Columbium, Cb) <= 5.5 %
<= 5.5 %
Phosphorous, P <= 0.015 %
<= 0.015 %
Silicon, Si <= 0.50 %
<= 0.50 %
Sulfur, S <= 0.015 %
<= 0.015 %
Tantalum, Ta <= 5.5 %
<= 5.5 %
Titanium, Ti 1.25 - 1.75 %
1.25 - 1.75 %