Chevron Phillips 6109 LLDPE Blown Film Resin, Butene Copolymer  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Butene, Film
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chevron Phillips 6109 LLDPE Blown Film Resin, Butene Copolymer  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Resin Type: Butene CopolymerCharacteristics: Good Stiffness at Thin Gauges, Good Drawdown, Can be used straight or blended with LDPE or HDPEApplications:Industrial Liners, Stretch Wrap, Garment Bags, Carrier Bags, CoextrusionsProcessing Conditions: Extruder 6.35 cm. Screw L/D Ratio 24:1. Die Opening 0.1905 cm. Blow-Up Ratio 2:1.Film properties below based on film thickness of 31.8 µm.Data provided by Chevron Chemical.
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
ASTM D1505
Melt Flow 0.90 g/10 min
0.90 g/10 min
Condition E; ASTM D 1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 525 %
525 %
ASTM D882
Film Elongation at Break, TD 675 %
675 %
ASTM D882
Secant Modulus, MD 0.220 GPa
31.9 ksi
ASTM D882
Secant Modulus, TD 0.270 GPa
39.2 ksi
ASTM D882
Coefficient of Friction 0.80
0.80
ASTM D1894
Elmendorf Tear Strength, MD 5.91 g/micron
150 g/mil
Notched; ASTM D1922
Elmendorf Tear Strength, TD 22.6 g/micron
575 g/mil
ASTM D1922
Dart Drop 2.40 g/micron
61.0 g/mil
F<sub>50</sub>; 1.5 in. dart/26 in. drop height; ASTM D 1709
Film Tensile Strength at Break, MD 35.0 MPa
5080 psi
ASTM D882
Film Tensile Strength at Break, TD 35.0 MPa
5080 psi
ASTM D882
Optical Properties Metric English Comments
Haze 12 %
12 %
ASTM D2457
Gloss 50 %
50 %
at 45°. ASTM D 2457
90 %
90 %
at 60°. ASTM D 2457
Processing Properties Metric English Comments
Melt Temperature 220 °C