Covestro Bayblend® FR 3021 Polycarbonate + ABS, Mineral Filled

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer Covestro
Trade Name Bayblend®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Bayblend® FR 3021 Polycarbonate + ABS, Mineral Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
15 % mineral filledinjection molding gradeincreased stiffnesstensile modulus = 4800 MPaVicat/B 120 temperature = 98 °CUL-listing 94 V-0 (1.5 mm) antimony-, chlorine- and bromine-free flame retardantglow wire test (GWFI): 960 °C (2.0 mm)no juicingAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
Physical Properties Metric English Comments
Density 1.28 g/cc
0.0462 lb/in³
ISO 1183
Water Absorption 0.50 %
0.50 %
Similar to ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
Similar to ISO 62
Melt Flow 17 g/10 min

@Load 5.00 kg,
Temperature 240 °C
17 g/10 min

@Load 11.0 lb,
Temperature 464 °F
estimated from MVR using room temperature density; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 65.0 MPa
9430 psi
ISO 527-1/-2
Elongation at Yield 3.0 %
3.0 %
ISO 527-1/-2
Tensile Modulus 4.80 GPa
696 ksi
ISO 527-1/-2
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 92.0 °C
198 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
ISO 75-1/-2
Vicat Softening Point 96.0 °C
205 °F
50°C/h 50N; ISO 306
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.0

@Frequency 1.00e+6 Hz
3.0

@Frequency 1.00e+6 Hz
IEC 60250
3.1

@Frequency 100 Hz
3.1

@Frequency 100 Hz
IEC 60250
Dielectric Strength 35.0 kV/mm
889 kV/in
IEC 60243-1
Dissipation Factor 0.0050

@Frequency 100 Hz
0.0050

@Frequency 100 Hz
IEC 60250
0.0070

@Frequency 1.00e+6 Hz
0.0070

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 275 V
275 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 240 °C
464 °F
Injection Molding; ISO 294
240 - 270 °C
464 - 518 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
80.0 °C
176 °F
Injection Molding; ISO 10724
Injection Velocity 240 mm/sec
9.45 in/sec
ISO 294
Descriptive Properties Value Comments
Availability Asia Pacific
Europe
India
Near East/Africa
South and Central America
Feature Release agent
Form Pellets
Process Injection Molding