Denka LCS Z6070 Thermoplastic Elastomer, Injection Molding Grade (general)

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer Denka
Trade Name LCS
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Denka LCS Z6070 Thermoplastic Elastomer, Injection Molding Grade (general).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
"DENKA LCS" combines low hardness with a rubber-like texture, having a low permanent compressive distortion/permanent elongation, and is a thermoplastic elastomer that closely resembles vulcanized rubber. It also offers advantages such as a high coefficient of friction, ease of lowering electrical resistance, and good energy-absorbing performance. ApplicationsFor use in automotive components such as weather strips, as well as architectural gaskets, electrical components, etc.
Physical Properties Metric English Comments
Density 1.15 g/cc
0.0415 lb/in³
JIS-Z-8807
Evaporation Loss 6.0 %
6.0 %
JIS-A-5756
Mechanical Properties Metric English Comments
Hardness, Shore A 70
70
JIS-K-6301
Tensile Strength at Break 13.734 MPa
1992.0 psi
JIS-K-6723
Elongation at Break 400 %
400 %
JIS-K-6723
100% Modulus 0.0027468 GPa
0.39840 ksi
JIS-K-6723
Tear Strength 36.3 kN/m
207 pli
kg/cm²; JIS-K-6301
Compression Set 38 %
38 %
70°C, 22hrs; JIS-K-6301
49 %
49 %
100°C, 70hrs; JIS-K-6301
Thermal Properties Metric English Comments
Minimum Service Temperature, Air -36.0 °C
-32.8 °F
JIS-K-6723
Descriptive Properties Value Comments
Heating: Retention Rate of Elongation, % 90
100°C x 120 hrs
Heating: Retention Rate of Tensile Strength, % 110
100°C x 120 hrs
Oil Resistance: Retention of Tensile Strength, % 100
70°C x 4hrs; JIS-K-6723
Oil Resistance: Retention Rate of Elongation, % 95
70°C x 4hrs; JIS-K-6723
Permanent Set, %, 100% 6
Permanent Set, %, 200% 12