Material Notes:
Essentially a thermoplastic elastomer with the characteristics of PVC resin and rubber, with excellent rubber-like elasticity. Offers excellent rubbery characteristics, such as permanent compressive distortion, rebound elasticity, etc. compared to soft PVC, and excellent bending strength and ozone resistance compared to rubberApplications[Automotive components]door moldingsweather-stripsglass run channelsside bumpersgasketsmud flapshead restsarm restssteering wheelstrimshift bar bootspedal pads[Construction material, manufacturing article home electric, appliance components]gasketsairtight materialscontainer packingpacking for vacuum cleanershosestubes[For electric wire]appliance cordscabtire
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
JIS-Z-8807
Evaporation Loss 2.8 %
2.8 %
JIS-A-5756
Mechanical Properties Metric English Comments
Hardness, Shore A 70
70
JIS-K-6301
Tensile Strength at Break 17.658 MPa
2561.1 psi
JIS-K-6723
Elongation at Break 335 %
335 %
JIS-K-6723
100% Modulus 0.006867 GPa
0.9960 ksi
JIS-K-6723
Resilience 32
32
JIS-K-6301
Compression Set 54 %
54 %
JIS-K-6301
Thermal Properties Metric English Comments
Minimum Service Temperature, Air -47.0 °C
-52.6 °F
JIS-K-6723
Descriptive Properties Value Comments
Bending Strength, Times, JIS-K-6301 over 100k
Heating: Retention Rate of Elongation, % 92
100°C x 120 hrs
Heating: Retention Rate of Tensile Strength, % 104
100°C x 120 hrs
Oil Resistance: Retention of Tensile Strength, % 95
JIS-K-6723
Oil Resistance: Retention Rate of Elongation, % 86
JIS-K-6723