Dow 751A Low Density Polyethylene Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Dow Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow 751A Low Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
A high additive film resin for general packaging applications For cast film extrusion A fast blooming resin for high speed bag conversion Complies with U.S. FDA 21 CFR 177.1520 (c) 2.1 Information provided by Dow
Physical Properties Metric English Comments
Density 0.9245 g/cc
0.03340 lb/in³
ASTM D792
Thickness 50.8 microns
2.00 mil
Melt Flow 6.4 g/10 min
6.4 g/10 min
ASTM D1238
Antiblock Level 2900 ppm
2900 ppm
Slip Level 2640 ppm
2640 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 13.85 MPa
2009 psi
ASTM D882
Film Tensile Strength at Yield, TD 11.42 MPa
1656 psi
ASTM D882
Film Elongation at Break, MD 146 %
146 %
ASTM D882
Film Elongation at Break, TD 441 %
441 %
ASTM D882
Impact 11
11
[ft-lbf/in<sup>3</sup>]; Puncture Resistance; Dow Method
951
951
[ft-lbf/in<sup>3</sup>]; Toughness MD; ASTM D882
1141
1141
[ft-lbf/in<sup>3</sup>]; Toughness TD; ASTM D882
Elmendorf Tear Strength MD 203 g
203 g
ASTM D1922
Elmendorf Tear Strength TD 102 g
102 g
ASTM D1922
Elmendorf Tear Strength, MD 3.996 g/micron
101.5 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 2.01 g/micron
51.0 g/mil
ASTM D1922
Dart Drop Test 25.0 g
0.0551 lb
Method A; ASTM D1709
Film Tensile Strength at Break, MD 32.4 MPa
4700 psi
ASTM D882
Film Tensile Strength at Break, TD 12.76 MPa
1851 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 113 °C
235 °F
Dow Method (DSC)
Vicat Softening Point 96.0 °C
205 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 4.4 %
4.4 %
ASTM D1003
Gloss 80 %
80 %
45°; ASTM D2457