DuPont Performance Polymers VTR 8650 (GBL-S) Peroxide Cured Fluoroelastomer (FKM) Formulation
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | DuPont Performance Polymers (Former DuPont Elastomers) |
| Trade Name | VTR |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers VTR 8650 (GBL-S) Peroxide Cured Fluoroelastomer (FKM) Formulation.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FormulationVTR 8650
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 60 @Temperature 121 °C |
60 @Temperature 250 °F |
ML-10 (gum) |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 69 | 69 | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Tensile Strength, Ultimate | 21.5 MPa | 3120 psi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Elongation at Break | 318 % | 318 % | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Modulus of Elasticity | 0.000600 GPa | 0.0870 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| 100% Modulus | 0.00410 GPa | 0.595 ksi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Compression Set | 15 % @Temperature 200 °C |
15 % @Temperature 392 °F |
Method B, O-rings 22 hr at 200°C (Post Cured 2 hr at 232°C) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | -17.0 °C | 1.40 °F | DSC, modulated, midpoint |