DuPont Vamac® GLS Sample Compound Vulcanizate Slab Cured

Category Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE)
Manufacturer DuPont Packaging and Industrial Polymers
Trade Name Vamac®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Vamac® GLS Sample Compound Vulcanizate Slab Cured.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Test slab is press cured for 5 minutes at 177°C and post cured for 4hrs at 175°C. Vulcanizate performance test data can help end-users evaluate the potential fitness of similar compounds for their own applications.Information provided by DuPont.
Mechanical Properties Metric English Comments
Hardness, Shore A 68
68
72
72
Air aged 7 days at 150°C
86
86
Air aged 14 days at 175°C
Tensile Strength, Ultimate 15.4 MPa
2230 psi
Air aged 14 days at 175°C
15.6 MPa
2260 psi
Air aged 7 days at 150°C
16.1 MPa
2340 psi
Elongation at Break 193 %
193 %
Air aged 14 days at 175°C
272 %
272 %
278 %
278 %
Air aged 7 days at 150°C
100% Modulus 0.00640 GPa
0.928 ksi
0.00680 GPa
0.986 ksi
Air aged 7 days at 150°C
0.00950 GPa
1.38 ksi
Air aged 14 days at 175°C
Tear Strength 34.0 kN/m
194 pli
Die C, at 23°C
Compression Set 20 %
20 %
70 hrs at 150°C, method B, plied
28 %
28 %
168 hrs at 150°C, method B, plied
Thermal Properties Metric English Comments
Glass Transition Temp, Tg -23.0 °C
-9.40 °F
By DSC
Descriptive Properties Value Comments
Armeen® 18D 0.5 parts
Diak No. 1 1.5 parts
DOTG Coaccelerator 4 parts
FEF Black(N550) 60 parts
Naugard® 445 antioxidant 2 parts
Stearic Acid 1.5 parts
TP-760 10 parts
Vamac® GLS 100 parts
Vanfre® VAM 1 part