ExxonMobil Bicor™ 25 ARW OPP Film

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Exxon Chemical
Trade Name Bicor™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Bicor™ 25 ARW OPP Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Bicor ARW is a two-side acrylic-coated OPP film designed for use in lamination and monoweb applications, especially for paper ream wrap. The acrylic-coated side with the higher COF is intended to be against the paper to ensure a tight wrap, whereas the side with the lower COF is intended as the outside surface. This film has broad seal range suitable for ream overwrap applications.Availability: Latin America, North America and South AmericaKey Features:Consistent COFRobust machinabilityExcellent optical propertiesGood hot slipExcellent stiffnessExcellent hot melt adhesionExcellent hot tack and seal strengthExcellent flavor and aroma barrierFeatures:Acrylic CoatedBroad seal RangeIn Lamination Lap SealableApplications:Paper Ream wrap Uses:Box Overwrap Flexible PackagingHFFS Flexible PackagingPre-made Bags – Flexible PackagingTobacco Overwrap Flexible PackagingVFFS Flexible PackagingProcessing Method: Inner Web Adhesive Lamination, Outer Web Adhesive Lamination and Surface Print UnsupportedInformation provided by ExxonMobil
Physical Properties Metric English Comments
Water Vapor Transmission 4.97 g/m²/day

@Temperature 38.0 °C
0.320 g/100 in²/day

@Temperature 100 °F
90% RH; ExxonMobil Method
Thickness 25.4 microns
1.00 mil
ExxonMobil Method
Coating Weight 22.7 g/m²
14.2 lb/ream
ExxonMobil Method
Mechanical Properties Metric English Comments
Coefficient of Friction 0.25
0.25
Slip Modified; ExxonMobil Method
0.52
0.52
Print; ExxonMobil Method
Film Tensile Strength at Break, MD 138 MPa
20000 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD 234 MPa
34000 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
Thermal Properties Metric English Comments
Shrinkage, MD 5.0 %

@Temperature 135 °C
5.0 %

@Temperature 275 °F
ExxonMobil Method
Shrinkage, TD 5.0 %

@Temperature 135 °C
5.0 %

@Temperature 275 °F
ExxonMobil Method
Optical Properties Metric English Comments
Haze 1.5 %
1.5 %
ExxonMobil Method
Gloss 86 %
86 %
45°; ExxonMobil Method
Descriptive Properties Value Comments
Crimp Seal MST 185°F
Acrylic/Acrylic
Crimp Seal Strength 500 g/in
240°F (116°C), 20 psi (0.1 MPa), 0.8 sec
Yield 30500 in2/lb