ExxonMobil Escorene™ FL 00309 Ethylene Vinyl Acetate Copolymer (European Grade)

Category Polymer , Thermoplastic , Ethylene Vinyl Acetate
Manufacturer Exxon Chemical
Trade Name Escorene™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene™ FL 00309 Ethylene Vinyl Acetate Copolymer (European Grade).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: FL 00309 is a copolymer of ethylene and vinyl acetate. Processing Conditions: Processing temperatures above 270°C (513°F) may cause resin degradation. Availability: Africa & Middle East and Europe Additive: Antiblock: NoSlip: NoThermal Stabilizer: No Applications:Cast FilmCo-Extrusion FilmsFood packagingInjection MoldingLamination FilmInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.929 g/cc
0.0336 lb/in³
ExxonMobil method
Vinyl Acetate Content 9.4 %
9.4 %
ExxonMobil method
Melt Flow 3.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 93

@Time 15.0 sec
93

@Time 0.00417 hour
Molded Properties; ISO 868
Tensile Strength at Break >= 0.689 MPa
>= 100 psi
Molded Properties; ISO 527-2/1A/100
Film Elongation at Break, MD 500 %
500 %
ASTM D882
Film Elongation at Break, TD 600 %
600 %
ASTM D882
Tensile Modulus 0.0758 GPa
11.0 ksi
Molded Properties; ISO 527-2/1
Elmendorf Tear Strength MD 80 g
80 g
ASTM D1922
Elmendorf Tear Strength TD 130 g
130 g
ASTM D1922
Dart Drop Test 360 g
0.794 lb
ASTM D1709A
Film Tensile Strength at Break, MD 24.8 MPa
3600 psi
ASTM D882
Film Tensile Strength at Break, TD 24.1 MPa
3500 psi
ASTM D882
1% Secant Modulus, MD 103 MPa
15000 psi
ASTM D882
1% Secant Modulus, TD 110 MPa
16000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point <= 205 °C
<= 401 °F
Peak Melting Point; ExxonMobil method
Vicat Softening Point 74.4 °C
166 °F
ASTM D1525
Descriptive Properties Value Comments
Blending Temperature 270