ExxonMobil Escorene™ FL 00714 Ethylene Vinyl Acetate Copolymer (European Grade)

Category Polymer , Thermoplastic , Ethylene Vinyl Acetate
Manufacturer Exxon Chemical
Trade Name Escorene™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene™ FL 00714 Ethylene Vinyl Acetate Copolymer (European Grade).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: FL 00714 is an easy processable grade for extrusion coating, co-extrusion coating and cast film. This grade offers excellent heat sealing characteristics and excellent optical properties.Processing Conditions: Excellent results are obtained in extrusion coating at 240°C (464°F) temperature range. Processing temperatures above 250°C (482°F) may cause resin degradation. FL 00714 should be fed into the extruder after LDPE of a similar or higher melt index. Machines should always be purged with LDPE or a suitable cleaning compound before shutdown.Availability: Africa & Middle East and Europe Additive: Antiblock: NoSlip: No Thermal Stabilizer: Yes Applications:Adhesive LaminationBarrier Food PackagingCling LayerCoextrusion CoatingDocument PlastificationExtrusion CoatingExtrusion LaminationFlexible Packaging Industrial PackagingInjection MoldingThermal LaminationInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.933 g/cc
0.0337 lb/in³
ExxonMobil method
Vinyl Acetate Content 14 %
14 %
ExxonMobil method
Melt Flow 7.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
7.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Neck In 7.11 cm

@Temperature 240 °C
2.80 in

@Temperature 464 °F
656 ft/min, constant output at 35 rpm; ExxonMobil Method
8.13 cm

@Temperature 240 °C
3.20 in

@Temperature 464 °F
328 ft/min, constant output at 35 rpm; ExxonMobil Method
Drawdown 5.00 m/s

@Temperature 240 °C
984 ft/min

@Temperature 464 °F
Constant output at 35 rpm; ExxonMobil Method
Mechanical Properties Metric English Comments
Hardness, Shore A 90

@Time 15.0 sec
90

@Time 0.00417 hour
Molded Properties; ISO 868
Tensile Strength at Break >= 0.689 MPa
>= 100 psi
Molded Properties; ISO 527-2/1A/100
Tensile Modulus 0.0510 GPa
7.40 ksi
Molded Properties; ISO 527-2/1
Thermal Properties Metric English Comments
Melting Point <= 190 °C
<= 374 °F
Peak Melting Point; ExxonMobil method
Vicat Softening Point 61.7 °C
143 °F
ASTM D1525
Descriptive Properties Value Comments
Blending Temperature 250